We report on the microwave surface resistance of two polycrystalline Mg11B2 samples; one consists of pristine material, the other has been irradiated at very high neutron fluence. It has already been reported that in the strongly irradiated sample the two gaps merge into a single value. The mw surface resistance has been measured in the linear regime as a function of the temperature and the DC magnetic field, at increasing and decreasing fields. The results obtained in the strongly irradiated sample are quite well justified in the framework of a generalized Coffey and Clem model, in which we take into account the field distribution inside the sample due to the critical state. The results obtained in the pristine sample show several anomalies, especially at low temperatures, which cannot be justified in the framework of standard models for the fluxon dynamics. Only at temperatures near Tc and for magnetic fields greater than 0.5Hc2(T) the experimental data can quantitatively be accounted for by the Coffey and Clem model, provided that the upper-critical-field anisotropy is taken into due account.
rate research
Read More
We report on the microwave surface resistance of melt-textured Y_1.6Ba_2.3Cu_3.3O_7-x samples, doped with different amount of B_2O_3 and, subsequently, irradiated by thermal neutrons at the fluence of 1.476 times 10^17 cm^-2. The microwave surface resistance has been measured as a function of temperature and DC magnetic field. The experimental results are quantitatively discussed in the framework of the Coffey and Clem theory, properly adapted to take into account the d-wave nature of cuprate superconductors. By fitting the experimental data at zero DC field, we have highlighted the effects of the induced defects in the general properties of the samples, including the intergranular region. The analysis of the results obtained at high DC fields allowed us to investigate the fluxon dynamics and deduce the depinning frequency; in particular, we have shown that the addition of B_2O_3 up to 0.1 wt% increases the effectiveness of the defects to hinder the fluxon motion induced by the microwave current.
The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being the breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high quality film growth for technical applications.
The magnetic-field-induced variations of the microwave surface resistance, R_s, have been investigated in ceramic Mg_{1-x}(LiAl)_xB_2, with x in the range 0.1 - 0.4. The measurements have been performed on increasing and decreasing the DC magnetic field, H_0, at fixed temperatures. At low temperatures, we have observed a magnetic hysteresis in the R_s(H_0) curves in all the investigated samples. On increasing the temperature, the range of H_0 in which the hysteretic behavior is visible shrinks; however, in the sample with x = 0.1 it is present up to temperatures close to T_c. We show that the field dependence of R_s can be quantitatively justified taking into account the critical-state effects on the fluxon lattice only in the sample with x = 0.4. On the contrary, in the samples with x < 0.4 the hysteresis exhibits an unusual shape, similar to that observed in others two-gap MgB_2 samples, which cannot be justified in the framework of the critical-state models.
We study the effect of neutron irradiation on the critical current density Jc of isotopically pure polycrystalline Mg11B2 samples. For fluences in the range 1017-1018 cm-2, Jc is enhanced and its dependence on magnetic field is significantly improved: we demonstrate that, in this regime, point-like pinning centers are effectively introduced in the system proportionally to the neutron fluence. Instead, for larger fluences, a strong suppression of the critical temperature accompanied by a decrease of both the upper critical field Bc2 and Jc is found.
The magnetic-field-induced variations of the microwave surface resistance have been investigated in a heavily neutron-irradiated MgB2 sample, in which the irradiation has caused the merging of the two gaps into a single value. The experimental results have been analyzed in the framework of the Coffey and Clem model. By fitting the experimental data, we have determined the field dependence of the depinning frequency, omega_0, at different values of the temperature. Although the pinning is not particularly effective, the value of omega_0 obtained at low temperatures is considerably higher than that observed in conventional low-temperature superconductors.