High energy milling of MgB2 pre-reacted powder renders the material largely amorphous through extreme mechanical deformation and is suitable for mechanically alloying MgB2 with dopants including carbon. Bulk samples of milled C and MgB2 powders subjected to hot isostatic pressing and Mg vapor annealing have achieved critical fields in excess of 32T and critical current density approaching 10^6 A/cm^2.