Register a new userCapping-induced suppression of annealing in Ga(1-x)Mn(x)As epilayers
60
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
We have studied the effects of capping ferromagnetic Ga(1-x)Mn(x)As epilayers with a thin layer of undoped GaAs, and we find that even a few monolayers of GaAs have a significant effect on the ferromagnetic properties. In particular, the presence of a capping layer only 10 monolayers thick completely suppresses the enhancement of the ferromagnetism associated with low temperature annealing. This result, which demonstrates that the surface of a Ga(1-x)Mn(x)As epilayer strongly affects the defect structure, has important implications for the incorporation of Ga(1-x)Mn(x)As into device heterostructures.
rate research
Read More
We have studied the field dependence of the magnetization in epilayers of the diluted magnetic semiconductor Ga(1-x)Mn(x)As for 0.0135 < x < 0.083. Measurements of the low temperature magnetization in fields up to 3 T show a significant deficit in the total moment below that expected for full saturation of all the Mn spins. These results suggest that the spin state of the non-ferromagnetic Mn spins is energetically well separated from the ferromagnetism of the bulk of the spins. We have also studied the coercive field (Hc) as a function of temperature and Mn concentration, finding that Hc decreases with increasing Mn concentration as predicted theoretically.
The dependence of the magnetic anisotropy of As-capped (Ga,Mn)As epilayers on the annealing parameters - temperature and time - has been investigated. A uniaxial magnetic anisotropy is evidenced, whose orientation with respect to the crystallographic axes changes upon annealing from [-110] for the as-grown samples to [110] for the annealed samples. Both cubic an uniaxial anisotropies are tightly linked to the concentration of charge carriers, the magnitude of which is controlled by the annealing process.
We have studied the depth-dependent magnetic and structural properties of as-grown and optimally annealed Ga[1-x]Mn[x]As films using polarized neutron reflectometry. In addition to increasing total magnetization, the annealing process was observed to produce a significantly more homogeneous distribution of the magnetization. This difference in the films is attributed to the redistribution of Mn at interstitial sites during the annealing process. Also, we have seen evidence of significant magnetization depletion at the surface of both as-grown and annealed films.
We have measured the magnetoresistance in a series of Ga$_{1-x}$Mn$_x$As samples with 0.033$le x le$ 0.053 for three mutually orthogonal orientations of the applied magnetic field. The spontaneous resistivity anisotropy (SRA) in these materials is negative (i.e. the sample resistance is higher when its magnetization is perpendicular to the measuring current than when the two are parallel) and has a magnitude on the order of 5% at temperatures near 10K and below. This stands in contrast to the results for most conventional magnetic materials where the SRA is considerably smaller in magnitude for those few cases in which a negative sign is observed. The magnitude of the SRA drops from its maximum at low temperatures to zero at T$_C$ in a manner that is consistent with mean field theory. These results should provide a significant test for emerging theories of transport in this new class of materials.
We report on the magnetic and the electronic properties of the prototype dilute magnetic semiconductor Ga$_{1-x}$Mn$_x$As using infrared (IR) spectroscopy. Trends in the ferromagnetic transition temperature $T_C$ with respect to the IR spectral weight are examined using a sum-rule analysis of IR conductivity spectra. We find non-monotonic behavior of trends in $T_C$ with the spectral weight to effective Mn ratio, which suggest a strong double-exchange component to the FM mechanism, and highlights the important role of impurity states and localization at the Fermi level. Spectroscopic features of the IR conductivity are tracked as they evolve with temperature, doping, annealing, As-antisite compensation, and are found only to be consistent with an Mn-induced IB scenario. Furthermore, our detailed exploration of these spectral features demonstrates that seemingly conflicting trends reported in the literature regarding a broad mid-IR resonance with respect to carrier density in Ga$_{1-x}$Mn$_x$As are in fact not contradictory. Our study thus provides a consistent experimental picture of the magnetic and electronic properties of Ga$_{1-x}$Mn$_x$As.