Structural properties of molten silicates from ab initio molecular-dynamics simulations: comparison between CaO-Al$_2$O$_3$-SiO$_2$ and SiO$_2$

121   0   0.0 ( 0 )
 Added by Magali Benoit
 Publication date 2001
  fields Physics
and research's language is English




Ask ChatGPT about the research

We present the results of first-principles molecular-dynamics simulations of molten silicates, based on the density functional formalism. In particular, the structural properties of a calcium aluminosilicate $ [$ CaO-Al$_2$O$_3$-SiO$_2$ $ ]$ melt are compared to those of a silica melt. The local structures of the two melts are in good agreement with the experimental understanding of these systems. In the calcium aluminosilicate melt, the number of non-bridging oxygens found is in excess of the number obtained from a simple stoichiometric prediction. In addition, the aluminum avoidance principle, which states that links between AlO$_4$ tetrahedra are absent or rare, is found to be violated. Defects such as 2-fold rings and 5-fold coordinated silicon atoms are found in comparable proportions in both liquids. However, in the calcium aluminosilicate melt, a larger proportion of oxygen atoms are 3-fold coordinated. In addition, 5-fold coordinated aluminum atoms are observed. Finally evidence of creation and anihilation of non-bridging oxygens is observed, with these oxygens being mostly connected to Si tetrahedra.



rate research

Read More

The impact of the inner structure and thermal history of planets on their observable features, such as luminosity or magnetic field, crucially depends on the poorly known heat and charge transport properties of their internal layers. The thermal and electric conductivities of different phases of water (liquid, solid, and super-ionic) occurring in the interior of ice giant planets, such as Uranus or Neptune, are evaluated from equilibrium ab initio molecular dynamics, leveraging recent progresses in the theory and data analysis of transport in extended systems. The implications of our findings on the evolution models of the ice giants are briefly discussed
A Molecular Dynamics (MD) study of static and dynamic properties of molten and glassy germanium dioxide is presented. The interactions between the atoms are modelled by the classical pair potential proposed by Oeffner and Elliott (OE) [Oeffner R D and Elliott S R 1998, Phys. Rev. B, 58, 14791]. We compare our results to experiments and previous simulations. In addition, an ab initio method, the so-called Car-Parrinello Molecular Dynamics (CPMD), is applied to check the accuracy of the structural properties, as obtained by the classical MD simulations with the OE potential. As in a similar study for SiO2, the structure predicted by CPMD is only slightly softer than that resulting from the classical MD. In contrast to earlier simulations, both the static structure and dynamic properties are in very good agreement with pertinent experimental data. MD simulations with the OE potential are also used to study the relaxation dynamics. As previously found for SiO2, for high temperatures the dynamics of molten GeO2 is compatible with a description in terms of mode coupling theory.
85 - T. Bryk , A.P. Seitsonen 2016
The collective dynamics in liquid water is an active research topic experimentally, theoretically and via simulations. Here, ab initio molecular dynamics simulations are reported in heavy and ordinary water at temperature 323.15 K, or 50$^circ$C. The simulations in heavy water were performed both with and without dispersion corrections. We found that the dispersion correction (DFT-D3) changes the relaxation of density-density time correlation functions from a slow, typical of a supercooled state, to exponential decay behaviour of regular liquids. This implies an essential reduction of the melting point of ice in simulations with DFT-D3. Analysis of longitudinal (L) and transverse (T) current spectral functions allowed us to estimate the dispersions of acoustic and optic collective excitations and to observe the L-T mixing effect. The dispersion correction shifts the L and T optic (O) modes to lower frequencies and provides by almost thirty per cent smaller gap between the longest-wavelength LO and TO excitations, which can be a consequence of a larger effective high-frequency dielectric permittivity in simulations with dispersion corrections. Simulation in ordinary water with the dispersion correction results in frequencies of optic excitations higher than in D$_2$O, and in a long-wavelength LO-TO gap of 24 ps$^{-1}$ (127 cm$^{-1}$).
Despite its interest for CMOS applications, Atomic Layer Deposition (ALD) of GeO$_{2}$ thin films, by itself or in combination with SiO$_{2}$, has not been widely investigated yet. Here we report the ALD growth of SiO$_{2}$/GeO$_{2}$ multilayers on Silicon substrates using a so far unreported Ge precursor. The characterization of multilayers with various periodicities reveals successful layer-by-layer growth with electron density contrast and absence of chemical intermixing, down to a periodicity of 2 atomic layers.
118 - Alaska Subedi 2021
I use first principles calculations to investigate the thermal conductivity of $beta$-In$_2$O$_3$ and compare the results with that of $alpha$-Al$_2$O$_3$, $beta$-Ga$_2$O$_3$, and KTaO$_3$. The calculated thermal conductivity of $beta$-In$_2$O$_3$ agrees well with the experimental data obtain recently, which found that the low-temperature thermal conductivity in this material can reach values above 1000 W/mK. I find that the calculated thermal conductivity of $beta$-Ga$_2$O$_3$ is larger than that of $beta$-In$_2$O$_3$ at all temperatures, which implies that $beta$-Ga$_2$O$_3$ should also exhibit high values of thermal conductivity at low temperatures. The thermal conductivity of KTaO$_3$ calculated ignoring the temperature-dependent phonon softening of low-frequency modes give high-temperature values similar that of $beta$-Ga$_2$O$_3$. However, the calculated thermal conductivity of KTaO$_3$ does not increase as steeply as that of the binary compounds at low temperatures, which results in KTaO$_3$ having the lowest low-temperature thermal conductivity despite having acoustic phonon velocities larger than that of $beta$-Ga$_2$O$_3$ and $beta$-In$_2$O$_3$. I attribute this to the fact that the acoustic phonon velocities at low frequencies in KTaO$_3$ is less uniformly distributed because its acoustic phonon branches are more dispersive compared to the binary oxides, which causes enhanced momentum loss even during the normal phonon-phonon scattering processes. I also calculate thermal diffusivity using the theoretically obtained thermal conductivity and heat capacity and find that all four materials exhibit the expected $T^{-1}$ behavior at high temperatures. Additionally, the calculated ratio of the average phonon scattering time to Planckian time is larger than the lower bound of 1 that has been observed empirically in numerous other materials.
comments
Fetching comments Fetching comments
Sign in to be able to follow your search criteria
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا