Register a new userCompeting ferromagnetic and antiferromagnetic interactions drive the magnetocaloric tunability in Gd55Co30NixAl15-x microwires
61
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
We have employed Gd55Co30NixAl15-x (x = 10, 5 and 0) amorphous microwires as a model system to unravel the impact of multiple magnetic interactions on the magnetism and the magnetocaloric behavior in Gd-alloy microwire systems. Our study shows that in addition to the RKKY ferromagnetic (FM) interaction (Gd-Gd), antiferromagnetic (AFM) interactions (Gd-Co, Gd-Ni) coexist and contribute to the magnetic and magnetocaloric response of the system. The dilution effect of Al element on the FM Gd-Gd interaction is responsible for the decrease of the Curie temperature (TC), whereas the increase of the saturation magnetization (MS) is originated from the reduced AFM Gd-Ni interaction. A thorough analysis of critical exponents suggests that the presence of the AFM interactions hinders the system to exhibit a long-range FM order below the TC. Adjusting these interactions is shown to preserve the large refrigerant capacity (RC) while tuning the TC over a wide temperature range, which is desirable for active magnetic refrigeration.
rate research
Read More
Inelastic neutron scattering measurements were performed on single crystals of the antiferromagnetic compound Mn5Si3 in order to investigate the relation between the spin dynamics and the magneto-thermodynamic properties. It is shown that among the two stable antiferromagnetic phases of this compound, the high temperature one has an unusual magnetic excitation spectrum where propagative spin-waves and diffuse spin-fluctuations coexist. Moreover, it is evidenced that the inverse magnetocaloric effect of Mn5Si3, the cooling by adiabatic magnetization, is associated with field induced spin-fluctuations.
We have investigated magnetocaloric effect in double perovskite Gd2NiMnO6 (GNMO) and Gd2CoMnO6 (GCMO) samples by magnetic and heat capacity measurements. Ferromagnetic ordering is observed at ~130 K (~112 K) in GNMO (GCMO), while the Gd exchange interactions seem to dominate for T < 20 K. In GCMO, below 50 K, an antiferromagnetic behaviour due to 3d-4f exchnage interaction is observed. A maximum entropy (-{Delta}SM) and adiabatic temperature change of ~35.5 J Kg-1 K-1 (~24 J Kg-1 K-1) and 10.5 K (6.5 K) is observed in GNMO (GCMO) for a magnetic field change of 7 T at low temperatures. Absence of magnetic and thermal hysteresis and their insulating nature make them promising for low temperature magnetic refrigeration.
We investigated the microwave properties of polymer based metacomposites containing hybridized parallel Fe- and Co-based microwire arrays. A dual-band left-handed feature was observed in the frequency bands of 1.5 to 5.5 GHz and 9 to 17 GHz, indicated by two transmission windows associated with ferromagnetic resonance of Fe-based microwires and long range dipolar resonance between the wire arrays. The plasma frequency after hybridization is significantly increased due to the enhanced effective diameter through the wire-wire interactions between the Fe- and Co- microwire couples. These results offer essential perspectives in designing the multi-band metamaterial for microwave applications such as sensors and cloaking devices.
We report on a novel class of nanocrystalline/amorphous Gd$_3$Ni/Gd$_{65}$Ni$_{35}$ composite microwires, which was created directly by melt-extraction through controlled solidification. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the formation of a biphase nanocrystalline/amorphous structure in these wires. Magnetic and magnetocaloric experiments indicate the large magnetic entropy change (-$Delta$SM ~9.64 J/kg K) and the large refrigerant capacity (RC ~742.1 J/kg) around the Curie temperature of ~120 K for a field change of 5 T. These values are ~1.5 times larger relative to its bulk counterpart, and are superior to other candidate materials being considered for active magnetic refrigeration in the liquid nitrogen temperature range.
The chiral clock spin-glass model with q=5 states, with both competing ferromagnetic-antiferromagnetic and left-right chiral frustrations, is studied in d=3 spatial dimensions by renormalization-group theory. The global phase diagram is calculated in temperature, antiferromagnetic bond concentration p, random chirality strength, and right-chirality concentration c. The system has a ferromagnetic phase, a multitude of different chiral phases, a chiral spin-glass phase, and a critical (algebraically) ordered phase. The ferromagnetic and chiral phases accumulate at the disordered phase boundary and form a spectrum of devils staircases, where different ordered phases characteristically intercede at all scales of phase-diagram space. Shallow and deep reentrances of the disordered phase, bordered by fragments of regular and temperature-inverted devils staircases, are seen. The extremely rich phase diagrams are presented as continuously and qualitatively changing videos.