Register a new userAnnealing of focused ion beam damage in gold microcrystals: An in situ Bragg coherent X-ray diffraction imaging study
92
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Focused ion beam (FIB) techniques are commonly used to machine, analyse and image materials at the micro- and nanoscale. However, FIB modifies the integrity of the sample by creating defects that cause lattice distortions. Methods have been developed to reduce FIB-induced strain, however these protocols need to be evaluated for their effectiveness. Here we use non-destructive Bragg coherent X-ray diffraction imaging to study the in situ annealing of FIB-milled gold microcrystals. We simultaneously measure two non-collinear reflections for two different crystals during a single annealing cycle, demonstrating the ability to reliably track the location of multiple Bragg peaks during thermal annealing. The thermal lattice expansion of each crystal is used to calculate the local temperature. This is compared to thermocouple readings, which are shown to be substantially affected by thermal resistance. To evaluate the annealing process, we analyse each reflection by considering facet area evolution, cross-correlation maps of displacement field and binarised morphology, and average strain plots. The crystals strain and morphology evolve with increasing temperature, which is likely to be caused by the diffusion of gallium in gold below ~280{deg}C and the self-diffusion of gold above ~280{deg}C. The majority of FIB-induced strains are removed by 380-410degree C, depending on which reflection is being considered. Our observations highlight the importance of measuring multiple reflections to unambiguously interpret material behaviour.
rate research
Read More
Mesocrystals are nanostructured materials consisting of individual nanocrystals having a preferred crystallographic orientation. On mesoscopic length scales, the properties of mesocrystals are strongly affected by structural heterogeneity. Here, we report the detailed structural characterization of a faceted mesocrystal grain self-assembled from 60 nm sized gold nanocubes. Using coherent X-ray diffraction imaging, we determined the structure of the mesocrystal with the resolution sufficient to resolve each gold nanoparticle. The reconstructed electron density of the gold mesocrystal reveals its intrinsic structural heterogeneity, including local deviations of lattice parameters, and the presence of internal defects. The strain distribution shows that the average superlattice obtained by angular X-ray cross-correlation analysis and the real, multidomain structure of a mesocrystal are very close to each other, with a deviation less than 10 percent. These results will provide an important impact to understanding of the fundamental principles of structuring and self-assembly including ensuing properties of mesocrystals.
Coherent X-ray beams with energies $geq 50$ keV can potentially enable three-dimensional imaging of atomic lattice distortion fields within individual crystallites in bulk polycrystalline materials through Bragg coherent diffraction imaging (BCDI). However, the undersampling of the diffraction signal due to Fourier space compression at high X-ray energies renders conventional phase retrieval algorithms unsuitable for three-dimensional reconstruction. To address this problem we utilize a phase retrieval method with a Fourier constraint specifically tailored for undersampled diffraction data measured with coarse-pitched detector pixels that bin the underlying signal. With our approach, we show that it is possible to reconstruct three-dimensional strained crystallites from an undersampled Bragg diffraction data set subject to pixel-area integration without having to physically upsample the diffraction signal. Using simulations and experimental results, we demonstrate that explicit modeling of Fourier space compression during phase retrieval provides a viable means by which to invert high-energy BCDI data, which is otherwise intractable.
Unique intensity features arising from dynamical diffraction arise in coherent x-ray nanobeam diffraction patterns of crystals having thicknesses larger than the x-ray extinction depth or exhibiting combinations of nanoscale and mesoscale features. We demonstrate that dynamical scattering effects can be accurately predicted using an optical model combined with the Darwin theory of dynamical x-ray diffraction. The model includes the highly divergent coherent x-ray nanobeams produced by Fresnel zone plate focusing optics and accounts for primary extinction, multiple scattering, and absorption. The simulation accurately reproduces the dynamical scattering features of experimental diffraction patterns acquired from a GaAs/AlGaAs epitaxial heterostructure on a GaAs (001) substrate.
There is considerable controversy about swift heavy ion (SHI) irradiation induced displacive phase transitions in thermally insulating oxides. We present here unambiguous evidence for tetragonal to monoclinic and rhombohedral to monoclinic phase transitions in BaTiO3 under swift heavy ion irradiation (120MeV 108Ag+9 ions) using in-situ x-ray powder diffraction (XRPD) studies. The anomalous splitting/broadening of 111/222pc, 200pc and 220pc pseudocubic peaks for fluences greater than 3*1012 ions/cm2 reveal structural changes before amorphization at higher fluences. Lebail analysis of XRPD profiles confirm that the monoclinic phase is of MA type in the Cm space group. Shear stress for the structural phase transition is estimated to be ~ 430MPa, which we believe is generated as a result of stopping of the SHI.
Bimetallic catalysts can undergo segregation or redistribution of the metals driven by oxidizing and reducing environments. Bragg coherent diffraction imaging (BCDI) was used to relate displacement fields to compositional distributions in crystalline Pt-Rh alloy nanoparticles. 3D images of internal composition showed that the radial distribution of compositions reverses partially between the surface shell and the core when gas flow changes between O2 and H2. Our observation suggests that the elemental segregation of nanoparticle catalysts should be highly active during heterogeneous catalysis and can be a controlling factor in synthesis of electrocatalysts. In addition, our study exemplifies applications of BCDI for in situ 3D imaging of internal equilibrium compositions in other bimetallic alloy nanoparticles.