Polycrystalline Heusler compounds Ni2Mn0.75Cu0.25Ga0.84Al0.16 with a martensitic transition between ferromagnetic phases and Ni2Mn0.70Cu0.30Ga0.84Al0.16 with a magnetostructural transformation were investigated by magnetization and thermal measurements, both as a function of temperature and magnetic field. The compound Ni2Mn0.75Cu0.25Ga0.84Al0.16 presents a large magnetocaloric effect among magnetically aligned structures and its causes are explored. In addition, Ni2Mn0.70Cu0.30Ga0.84Al0.16 shows very high, although irreversible, entropy and adiabatic temperature change at room temperature under a magnetic field change 0-1 T. Improved refrigerant capacity is also a highlight of the 30% Cu material when compared to similar Ni2MnGa-based alloys.