We evaluate the effect of mechanical exfoliation of van der Waals materials on crystallographic orientations of the resulting flakes. Flakes originating from a single crystal of graphite, whose orientation is confirmed using STM, are studied using facet orientations and electron back-scatter diffraction (EBSD). While facets exhibit a wide distribution of angles after a single round of exfoliation ($ sigma approx 5^o $), EBSD shows that the true crystallographic orientations are more narrowly distributed ($ sigma approx 1.5^o $), and facets have an approximately error from the true orientation. Furthermore, we find that the majority of graphite fractures are along armchair lines, and that the cleavage process results in an increase of the zigzag lines portion. Our results place values on the rotation caused by a single round of the exfoliation process, and suggest that when a 1-2 degree precision is necessary, the orientation of a flake can be gauged by the orientation of the macroscopic single crystal from which it was exfoliated.