Dielectric Screening by 2D Substrates

76   0   0.0 ( 0 )
 Added by Keian Noori
 Publication date 2020
  fields Physics
and research's language is English




Ask ChatGPT about the research

Two-dimensional (2D) materials are increasingly being used as active components in nanoscale devices. Many interesting properties of 2D materials stem from the reduced and highly non-local electronic screening in two dimensions. While electronic screening within 2D materials has been studied extensively, the question still remains of how 2D substrates screen charge perturbations or electronic excitations adjacent to them. Thickness-dependent dielectric screening properties have recently been studied using electrostatic force microscopy (EFM) experiments. However, it was suggested that some of the thickness-dependent trends were due to extrinsic effects. Similarly, Kelvin probe measurements (KPM) indicate that charge fluctuations are reduced when BN slabs are placed on SiO$_2$, but it is unclear if this effect is due to intrinsic screening from BN. In this work, we use first principles calculations to study the fully non-local dielectric screening properties of 2D material substrates. Our simulations give results in good qualitative agreement with those from EFM experiments, for hexagonal boron nitride (BN), graphene and MoS$_2$, indicating that the experimentally observed thickness-dependent screening effects are intrinsic to the 2D materials. We further investigate explicitly the role of BN in lowering charge potential fluctuations arising from charge impurities on an underlying SiO$_2$ substrate, as observed in the KPM experiments. 2D material substrates can also dramatically change the HOMO-LUMO gaps of adsorbates, especially for small molecules, such as benzene. We propose a reliable and very quick method to predict the HOMO-LUMO gap of small physisorbed molecules on 2D and 3D substrates, using only the band gap of the substrate and the gas phase gap of the molecule.



rate research

Read More

A method was developed to calculate the free energy of 2D materials on substrates and was demonstrated by the system of graphene and {gamma}-graphyne on copper substrate. The method works at least 3 orders faster than state-of-the-art algorithms, and the accuracy was tested by molecular dynamics simulations, showing that the precision for calculations of the internal energy achieves up to 0.03% in a temperature range from 100 to 1300K. As expected, the calculated the free energy of a graphene sheet on Cu (111) or Ni (111) surface in a temperature range up to 3000K is always smaller than the one of a {gamma}-graphyne sheet with the same number of C atoms, which is consistent with the fact that growth of graphene on the substrates is much easier than {gamma}-graphyne.
To understand the band bending caused by metal contacts, we study the potential and charge density induced in graphene in response to contact with a metal strip. We find that the screening is weak by comparison with a normal metal as a consequence of the ultra-relativistic nature of the electron spectrum near the Fermi energy. The induced potential decays with the distance from the metal contact as x^{-1/2} and x^{-1} for undoped and doped graphene, respectively, breaking its spatial homogeneity. In the contact region the metal contact can give rise to the formation of a p-p, n-n, p-n junction (or with additional gating or impurity doping, even a p-n-p junction) that contributes to the overall resistance of the graphene sample, destroying its electron-hole symmetry. Using the work functions of metal-covered graphene recently calculated by Khomyakov et al. [Phys. Rev. B 79, 195425 (2009)] we predict the boundary potential and junction type for different metal contacts.
The graphene-enhanced Raman scattering of Rhodamine 6G molecules on pristine, fluorinated and 4-nitrophenyl functionalized graphene substrates was studied. The uniformity of the Raman signal enhancement was studied by making large Raman maps. The relative enhancement of the Raman signal is demonstrated to be dependent on the functional groups, which was rationalized by the different doping levels of pristine, fluorinated and 4-nitrophenyl functionalized graphene substrates. The impact of the Fermi energy of graphene and the phonon energy of the molecules was considered together for the first time in order to explain the enhancement. Such approach enables to understand the enhancement without assuming anything about the uniformity of the molecules on the graphene surface. The agreement between the theory and our measured data was further demonstrated by varying excitation energy.
Large area nickel antidot arrays with density up to 10^10 /cm^2 have been fabricated by depositing nickel onto anodic aluminum oxide membranes that contain lattices of nanopores. Electron microscopy images show a high degree of order of the antidot arrays. Various sizes and shapes of the antidots were observed with increasing thickness of the deposited nickel. New features appear in the antidot arrays in both magnetization and transport measurements when the external magnetic field is parallel to the current direction, including an enhancement and a nonmonotonous field dependence of the magnetoresistance, larger values of the coercive field and remanence moment, and smaller saturation field.
The paper concerns the nanopowder high-speed, $10^4$ - $10^9$ s${}^{-1}$, compaction processes modeling by a two-dimensional granular dynamics method. Nanoparticles interaction, in addition to known contact laws, included dispersive attraction, formation of a strong interparticle bonding (powder agglomeration) as well as the forces caused by viscous stresses in the contact region. For different densification rates, the pressure vs. density curves (densification curves) were calculated. Relaxation of the stresses after the compression stage was analyzed as well. The densification curves analysis allowed us to suggest the dependence of compaction pressure as a function of strain rate. It was found that in contrast to the plastic flow of metals, where the yield strength is proportional to the logarithm of the strain rate, the power-law dependence of applied pressure on the strain rate as $ppropto v^{1/4}$ was established for the modeled nanosized powders.