The effects of hydrogen incorporation into beta-Ga2O3 thin films have been investigated by chemical, electrical and optical characterization techniques. Hydrogen incorporation was achieved by remote plasma doping without any structural alterations of the film; however, X-ray photoemission reveals major changes in the oxygen chemical environment. Depth-resolved cathodoluminescence (CL) reveals that the near-surface region of the H-doped Ga2O3 film exhibits a distinct red luminescence (RL) band at 1.9 eV. The emergence of the H-related RL band is accompanied by an enhancement in the electrical conductivity of the film by an order of magnitude. Temperature-resolved CL points to the formation of abundant H-related donors with a binding energy of 28 +/- 4 meV. The RL emission is attributed to shallow donor-deep acceptor pair recombination, where the acceptor is a VGa-H complex and the shallow donor is interstitial H. The binding energy of the VGa-H complex, based on our experimental considerations, is consistent with the computational results by Varley et al [J. Phys.: Condens. Matter, 23, 334212, 2011].
rate research
Read More
Experimental and computer-modeling studies of spectral properties of crystalline AgCl doped with metal bismuth or bismuth chloride are performed. Broad near-IR luminescence band in the 0.8--1.2mkm range with time dependence described by two exponential components corresponding to the lifetimes of 1.5 and 10.3mks is excited mainly by 0.39--0.44mkm radiation. Computer modeling of probable Bi-related centers in AgCl lattice is performed. On the basis of experimental and calculation data a conclusion is drawn that the IR luminescence can be caused by Bi^+ ion centers substituted for Ag^+ ions.
Optically-detected magnetic resonance (ODMR) and positron annihilation spectroscopy (PAS) experiments have been employed to study magnesium-doped GaN layers grown by metal-organic vapor phase epitaxy. As the Mg doping level is changed, the combined experiments reveal a strong correlation between the vacancy concentrations and the intensity of the red photoluminescence band at 1.8 eV. The analysis provides strong evidence that the emission is due to recombination in which electrons both from effective mass donors and from deeper donors recombine with deep centers, the deep centers being vacancy-related defects.
The quasi-static anisotropic permittivity parameters of electrically insulating gallium oxide (beta-Ga2O3) were determined by terahertz spectroscopy. Polarization-resolved frequency domain spectroscopy in the spectral range from 200 GHz to 1 THz was carried out on bulk crystals along different orientations. Principal directions for permittivity were determined along crystallographic axes c, and b, and reciprocal lattice direction a*. No significant frequency dispersion in the real part of dielectric permittivity was observed in the measured spectral range. Our results are in excellent agreement with recent radio-frequency capacitance measurements as well as with extrapolations from recent infrared measurements of phonon mode and high frequency contributions, and close the knowledge gap for these parameters in the terahertz spectral range. Our results are important for applications of beta-Ga2O3 in high-frequency electronic devices
A comparative first-principles study of possible bismuth-related centers in TlCl and CsI crystals is performed and the results of computer modeling are compared with the experimental data. The calculated spectral properties of the bismuth centers suggest that the IR luminescence observed in TlCl:Bi is most likely caused by Bi--Vac(Cl) centers (Bi^+ ion in thallium site and a negatively charged chlorine vacancy in the nearest anion site). On the contrary, Bi^+ substitutional ions and Bi_2^+ dimers are most likely responsible for the IR luminescence observed in CsI:Bi.
Experimental and theoretical studies of spectral properties of chalcogenide Ge-S and As-Ge-S glasses and fibers are performed. A broad infrared (IR) luminescence band which covers the 1.2-2.3~$mu$m range with a lifetime about 6~$mu$s is discovered. Similar luminescence is also present in optical fibers drawn from these glasses. Arsenic addition to Ge-S glass significantly enhances both its resistance to crystallization and the intensity of the luminescence. Computer modeling of Bi-related centers shows that interstitial Bi$^+$ ions adjacent to negatively charged S vacancies are most likely responsible for the IR luminescence.