Despite decades of extensive research on mechanical properties of diamond, much remains to be understood in term of plastic deformation mechanisms due to the poor deformability at room temperature. In a recent work in Advanced Materials, it was claimed that room-temperature plasticity occurred in <001>-oriented single-crystal diamond nanopillars based on observation of unrecovered deformation inside scanning electron microscope. The plastic deformation was suggested to be mediated by a phase transition from sp3 carbon to an O8-carbon phase by molecular dynamics simulations. By comparison, our in-situ transmission electron microscopy study reveals that the room-temperature plasticity can be carried out by dislocation slip in both <100> and <111>-oriented diamond nanopillars. The brittle-to-ductile transition is highly dependent on the stress state. We note that the surface structure may play a significant role in the deformation mechanisms as the incipient plasticity always occurs from the surface region in nanoscale diamonds.