Lithium niobate is a multi-functional material with wide reaching applications in acoustics, optics, and electronics. Commercial applications for lithium niobate require high crystalline quality currently limited to bulk and ion sliced material. Thin film lithium niobate is an attractive option for a variety of integrated devices, but the research effort has been stagnant due to poor material quality. Both lattice matched and mismatched lithium niobate are grown by molecular beam epitaxy (MBE) and studied to understand the role of substrate and temperature on nucleation conditions and material quality. Growth on sapphire produces partially coalesced columnar grains with atomically flat plateaus and no twin planes. A symmetric rocking curve shows a narrow linewidth with a full width at half-maximum (FWHM) of 8.6 arcsec (0.0024{deg}) which is comparable to the 5.8 arcsec rocking curve FWHM of the substrate, while the film asymmetric rocking curve is 510 arcsec FWHM. These values indicate that the individual grains are relatively free of long-range disorder detectable by x-ray diffraction (XRD) with minimal measurable tilt and twist and represents the highest structural quality epitaxial material grown on lattice mismatched sapphire without twin planes. Lithium niobate is also grown on lithium tantalate producing high quality coalesced material without twin planes and with a symmetric rocking curve of 193 arcsec, which is nearly equal to the substrate rocking curve of 194 arcsec. The surface morphology of lithium niobate on lithium tantalate is shown to be atomically flat by atomic force microscopy (AFM).
rate research
Read More
In a combined experimental and theoretical study, we investigate the influence of the material source arrangement in a molecular beam epitaxy (MBE) system on the growth of nanowire (NW) core-shell structures. In particular, we study the shell growth of GaN around GaN template NWs under the boundary condition that Ga and N do not impinge on a given sidewall facet at the same time. Our experiments with different V/III ratios and substrate temperatures show that obtaining shells with homogeneous thickness along the whole NW length is not straightforward. Analyzing in detail the shell morphology with and without substrate rotation, we find that the different azimuthal angles of the sources have a major impact on the Ga adatom kinetics and the final shell morphology. On the basis of these experimental results, we develop a diffusion model which takes into account different NW facets and the substrate. The model allows to describe well the experimental shell profiles and predicts that homogeneous shell growth can be achieved if the Ga and N source are arranged next to each other or for very high rotation speeds. Moreover, the modeling reveals that the growth on a given side facet can be categorized within one rotation in four different phases: the Ga wetting phase, the metal-rich growth phase, the N-rich growth phase, and the dissociation phase. The striking difference to growth processes on planar samples is that, in our case, diffusion takes place between different regions, i.e. the sidewall vs. the top facet and substrate, out of which on one N impinges not continuously, resulting in complex gradients in chemical potential that are modulated in time by substrate rotation. The comprehensiveness of our model provides a deep understanding of diffusion processes and the resulting adatom concentration, and could be applied to other 3D structures and material systems
We report growth of superconducting Sr2RuO4 films by oxide molecular beam epitaxy (MBE). Careful tuning of the Ru flux with an electron beam evaporator enables us to optimize growth conditions including the Ru/Sr flux ratio and also to investigate stoichiometry effects on the structural and transport properties. The highest onset transition temperature of about 1.1 K is observed for films grown in a slightly Ru-rich flux condition in order to suppress Ru deficiency. The realization of superconducting Sr2RuO4 films via oxide MBE opens up a new route to study the unconventional superconductivity of this material.
The role of stoichiometry and growth temperature in the preferential nucleation of material phases in the Li-Nb-O family are explored yielding an empirical growth phase diagram. It is shown that while single parameter variation often produces multi-phase films, combining substrate temperature control with the previously published lithium flux limited growth allows the repeatable growth of high quality single crystalline films of many different oxide phases. Higher temperatures (800-1050 {deg}C) than normally used in MBE were necessary to achieve high quality materials. At these temperatures the desorption of surface species is shown to play an important role in film composition. Using this method single phase films of NbO, NbO$_{2}$, LiNbO$_{2}$, Li$_{3}$NbO$_{4}$, LiNbO$_{3}$, and LiNb$_{3}$O$_{8}$ have been achieved in the same growth system, all on c-plane sapphire. Finally, the future of these films in functional oxide heterostructures is briefly discussed.
We report the successful growth of tetragonal FeS film with one or two unit-cell (UC) thickness on SrTiO3(001) substrate by molecular beam epitaxy. Large lattice constant mismatch with the substrate leads to high density of defects in single UC FeS, while it has been significantly reduced in double UC thick film due to the lattice relaxation. The scanning tunneling spectra on the surface of FeS thin film reveal the electronic doping effect of single UC FeS from the substrate. In addition, at the Fermi level, the energy gaps of approximate 1.5 meV are observed in films of both thicknesses at 4.6 K and below. The absence of coherence peaks of gap spectra may be related to the preformed Cooper-pairs without phase coherence.
We report on the epitaxial growth and surface structure of infinite-layer cuprate Sr1-xNdxCuO2 films on SrTiO3(001) substrates by combining ozone-assisted molecular beam epitaxy and in situ scanning tunneling microscopy. Careful substrate temperature and flux control has been used to achieve single-phase, stoichiometric, and c-axis oriented films. The surface of the films is usually characterized by a mixed CuO2 surface and gridlike superstructure. The superstructure exhibits a periodicity of 3.47 nm that corresponds to a coincidence lattice between the overlayer peroxide SrO2 and underlying CuO2 plane, and gives rise to a conductance spectrum that is distinct from the Mott-Hubbard band structure of CuO2. At a higher Nd composition x > 0.1, a (2 x 2) surface characteristic of the hole-doped CuO2 emerges, which we ascribe to the intake of apical oxygens in the intervening Sr planes.