We have discovered a new compound of the composition ScPd2Al3 crystallizing in unknown structure type. Moreover, ScPd2Al3 reveals polymorphism. We have found an orthorhombic crystal structure at room temperature and a high temperature cubic phase. The polymorphic phases are separated by a reversible first order transition at 1053{deg}C with a hysteresis of 19{deg}C. ScPd2Al3 exists as a very stable intermetallic phase just in the vicinity of the icosahedral quasicrystal Tsai-type i-phase Al54Pd30Sc16.