Growth of perovskite oxide thin films on Si in crystalline form has long been a critical obstacle for the integration of multifunctional oxides into Si-based technologies. In this study, we propose pulsed laser deposition of a crystalline SrTiO3 thin film on a Si using graphene substrate. The SrTiO3 thin film on graphene has a highly (00l)-oriented crystalline structure which results from the partial epitaxy. Moreover, graphene promotes a sharp interface by highly suppressing the chemical intermixing. The important role of graphene as a 2D substrate and diffusion barrier allows expansion of device applications based on functional complex oxides.
rate research
Read More
Strain engineering with different substrate facets is promising for tuning functional properties of thin film perovskite oxides. By choice of facet, different surface symmetries and chemical bond directions for epitaxial interfaces can be tailored. Here, preparation of well-defined pseudo-cubic (111)-oriented orthorhombic substrates of DyScO3 , GdScO3 , and NdGaO3 is reported. The choice of orthorhombic facet, (011)o or (101)o , both corresponding to pseudo-cubic (111)pc , gives vicinal surfaces with single or double (111pc layer terrace step heights, respectively, impacting subsequent thin film growth. Orthorhombic LaFeO3 epitaxy on the (101)o facet reveals a distinction between alternating (111)pc layers, both during and after growth. The observed differences are explained based on the oxygen octahedral tilt pattern relative to the two orthorhombic (111)pc surfaces. This robust structural detail in the orthorhombic perovskite oxides enables utilisation of different (111)pc facets for property engineering, through polyhedral connectivity control and cation coordination at epitaxial interfaces.
Multiferroic BiFeO3 (BFO) thin film exhibiting desired ferroelectric and enhanced magnetic properties was grown on La0.67Sr0.33MnO3 (LSMO) buffered Pt/TiO2/SiO2/Si substrates by off-axis RF magnetic sputtering, where a highly (111)-oriented texture was obtained. The BFO/LSMO thin film exhibits excellent ferroelectric and dielectric behaviors (2Pr ~210.7 {mu}C/cm2, 2Ec~435 kV/cm, {epsilon}r ~116.8, and tan{delta} ~ 2.7% at 1 kHz), together with a long fatigue endurance up to 1010 switching cycles at amplitude of 300 kV/cm. An enhancement in magnetic behavior was also observed with Ms=89.5 emu/cm3, which is largely contributed from the magnetic layer of LSMO. The coexistence of ferroelectric and ferromagnetic properties in the double layered BFO/LSMO thin film makes it a promising candidate system for applications where the magnetoelectric behavior is required.
The surface termination of (100)-oriented LaAlO3 (LAO) single crystals was examined by atomic force microscopy and optimized to produce a single-terminated atomically flat surface by annealing. Then the atomically flat STO film was achieved on a single-terminated LAO substrate, which is expected to be similar to the n-type interface of two-dimensional electron gas (2DEG), i.e., (LaO)-(TiO2). Particularly, that can serve as a mirror structure for the typical 2DEG heterostructure to further clarify the origin of 2DEG. This newly developed interface was determined to be highly insulating. Additionally, this study demonstrates an approach to achieve atomically flat film growth based on LAO substrates.
The stoichiometric 111 iron-based superconductor, LiFeAs, has attacted great research interest in recent years. For the first time, we have successfully grown LiFeAs thin film by molecular beam epitaxy (MBE) on SrTiO3(001) substrate, and studied the interfacial growth behavior by reflection high energy electron diffraction (RHEED) and low-temperature scanning tunneling microscope (LT-STM). The effects of substrate temperature and Li/Fe flux ratio were investigated. Uniform LiFeAs film as thin as 3 quintuple-layer (QL) is formed. Superconducting gap appears in LiFeAs films thicker than 4 QL at 4.7 K. When the film is thicker than 13 QL, the superconducting gap determined by the distance between coherence peaks is about 7 meV, close to the value of bulk material. The ex situ transport measurement of thick LiFeAs film shows a sharp superconducting transition around 16 K. The upper critical field, Hc2(0)=13.0 T, is estimated from the temperature dependent magnetoresistance. The precise thickness and quality control of LiFeAs film paves the road of growing similar ultrathin iron arsenide films.
We report a scalable approach to synthesize a large-area (up to 4 mm) thin black phosphorus (BP) film on a flexible substrate. We first deposited a red phosphorus (RP) thin-film on a flexible polyester substrate, followed by its conversion to BP in a high-pressure multi-anvil cell at room temperature. Raman spectroscopy and transmission electron microscopy measurements confirmed the formation of a nano-crystalline BP thin-film with a thickness of around 40 nm. Optical characterization indicates a bandgap of around 0.28 eV in the converted BP, similar to the bandgap measured in exfoliated thin-films. Thin-film BP transistors exhibit a field-effect mobility of around 0.5 cm2/Vs, which can probably be further enhanced by the optimization of the conversion process at elevated temperatures. Our work opens the avenue for the future demonstration of large-scale, high quality thin-film black phosphorus.