Register a new userLow Gilbert damping in Co2FeSi and Fe2CoSi films
83
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Thin highly textured Fe$_{mathrm{1+x}}$Co$_{mathrm{2-x}}$Si ($0 leq$ x $leq 1$) films were prepared on MgO (001) substrates by magnetron co-sputtering. The magneto-optic Kerr effect (MOKE) and ferromagnetic resonance (FMR) measurements were used to investigate the composition dependence of the magnetization, the magnetic anisotropy, the gyromagnetic ratio and the relaxation of the films. The effective magnetization for the thin Fe$_{mathrm{1+x}}$Co$_{mathrm{2-x}}$Si films, determined by FMR measurements, are consistent with the Slater Pauling prediction. Both MOKE and FMR measurements reveal a pronounced fourfold anisotropy distribution for all films. In addition we found a strong influence of the stoichiometry on the anisotropy as the cubic anisotropy strongly increases with increasing Fe concentration. The gyromagnetic ratio is only weakly dependent on the composition. We find low Gilbert damping parameters for all films with values down to $0.0012pm0.00012$ for Fe$_{1.75}$Co$_{1.25}$Si. The effective damping parameter for Co$_2$FeSi is found to be $0.0018pm 0.0004$. We also find a pronounced anisotropic relaxation, which indicates significant contributions of two-magnon scattering processes that is strongest along the easy axes of the films. This makes thin Fe$_{mathrm{1+x}}$Co$_{mathrm{2-x}}$Si films ideal materials for the application in STT-MRAM devices.
rate research
Read More
Tailoring Gilbert damping of metallic ferromagnetic thin films is one of the central interests in spintronics applications. Here we report a giant Gilbert damping anisotropy in epitaxial Co$_{50}$Fe$_{50}$ thin film with a maximum-minimum damping ratio of 400 %, determined by broadband spin-torque as well as inductive ferromagnetic resonance. We conclude that the origin of this damping anisotropy is the variation of the spin orbit coupling for different magnetization orientations in the cubic lattice, which is further corroborate from the magnitude of the anisotropic magnetoresistance in Co$_{50}$Fe$_{50}$.
We report on broadband ferromagnetic resonance linewidth measurements performed on epitaxial Heusler thin films. A large and anisotropic two-magnon scattering linewidth broadening is observed for measurements with the magnetization lying in the film plane, while linewidth measurements with the magnetization saturated perpendicular to the sample plane reveal low Gilbert damping constants of $(1.5pm0.1)times 10^{-3}$, $(1.8pm0.2)times 10^{-3}$, and $<8times 10^{-4}$ for Co$_2$MnSi/MgO, Co$_2$MnAl/MgO, and Co$_2$FeAl/MgO, respectively. The in-plane measurements are fit to a model combining Gilbert and two-magnon scattering contributions to the linewidth, revealing a characteristic disorder lengthscale of 10-100 nm.
The Gilbert damping of ferromagnetic materials is arguably the most important but least understood phenomenological parameter that dictates real-time magnetization dynamics. Understanding the physical origin of the Gilbert damping is highly relevant to developing future fast switching spintronics devices such as magnetic sensors and magnetic random access memory. Here, we report an experimental study of temperature-dependent Gilbert damping in permalloy (Py) thin films of varying thicknesses by ferromagnetic resonance. From the thickness dependence, two independent contributions to the Gilbert damping are identified, namely bulk damping and surface damping. Of particular interest, bulk damping decreases monotonically as the temperature decreases, while surface damping shows an enhancement peak at the temperature of ~50 K. These results provide an important insight to the physical origin of the Gilbert damping in ultrathin magnetic films.
We report an enhanced magnetoelastic contribution to the Gilbert damping in highly magnetostrictive Fe$_{0.7}$Ga$_{0.3}$ thin films. This effect is mitigated for perpendicular-to-plane fields, leading to a large anisotropy of the Gilbert damping in all of the films (up to a factor of 10 at room temperature). These claims are supported by broadband measurements of the ferromagnetic resonance linewidths over a range of temperatures (5 to 400 K), which serve to elucidate the effect of both the magnetostriction and phonon relaxation on the magnetoelastic Gilbert damping.
The effects of rhenium doping in the range 0 to 10 atomic percent on the static and dynamic magnetic properties of Fe65Co35 thin films have been studied experimentally as well as with first principles electronic structure calculations focusing on the change of the saturation magnetization and the Gilbert damping parameter. Both experimental and theoretical results show that the saturation magnetization decreases with increasing Re doping level, while at the same time Gilbert damping parameter increases. The experimental low temperature saturation magnetic induction exhibits a 29 percent decrease, from 2.31 T to 1.64 T, in the investigated doping concentration range, which is more than predicted by the theoretical calculations. The room temperature value of the damping parameter obtained from ferromagnetic resonance measurements, correcting for extrinsic contributions to the damping, is for the undoped sample 0.0027, which is close to the theoretically calculated Gilbert damping parameter. With 10 atomic percent Re doping, the damping parameter increases to 0.0090, which is in good agreement with the theoretical value of 0.0073. The increase in damping parameter with Re doping is explained by the increase in density of states at Fermi level, mostly contributed by the spin-up channel of Re. Moreover, both experimental and theoretical values for the damping parameter are observed to be weakly decreasing with decreasing temperature.