Improvement of the superconducting properties of polycrystalline FeSe by silver addition


Abstract in English

We investigated the influence of different Ag additions (up to 10 wt %) on the superconducting properties of FeSe0.94. The structural investigations (XRD and SEM) indicated that Ag is present in three different forms. Ag at grain boundaries supports the excellent intergrain connections and reduces superconducting transition width to values smaller than 1K at B=0 and smaller than 2.74 K at B=14 T. Ag insertion in the crystal lattice unit cell provides additional carriers and changes the electron hole imbalance in FeSe0.94. This results in an increase in the magnetoresistive effect (MR) and critical temperature (Tc). Reacted Ag forms a small amount (~1%) of Ag2Se impurity phase, which may increase the pinning energy in comparison with that of the undoped sample. The enhanced upper critical field (Bc2) is also a result of the increased impurity scattering. Thus, unlike cuprates Ag addition enhances the Tc, Bc2, pinning energy and MR making the properties of polycrystalline FeSe0.94 similar to those of single crystals.

Download