Effect of L-threonine (LT) doping on crystalline perfection, second harmonic generation (SHG) efficiency, optical transparency and laser damage threshold (LDT) in potassium dihydrogen phosphate (KDP) crystals grown by slow evaporation solution technique (SEST) has been investigated. The influence of doping on growth rate and morphology of the grown crystals has also been studied. Powder X-ray diffraction data confirms the crystal structure of KDP and shows a systematic variation in intensity of diffraction peaks in correlation with morphology due to varying LT concentration. No extra phase formation was observed which is further confirmed by Fourier Transform (FT) Raman studies. High-resolution X-ray diffraction curves indicate that crystalline perfection has been improved to a great extent at low concentrations with a maximum perfection at 1 mol% doping. At higher concentrations (5 to 10 mol%), it is slightly reduced due to excess incorporation of dopants at the interstitial sites of the crystalline matrix. LDT has been increased considerably with increase in doping concentration, whereas SHG efficiency was found to be maximum at 1 mol% in correlation with crystalline. The optical transparency for doped crystals has been increased as compared to that of pure KDP with a maximum value at 1 mol% doping.
Download