In glass, starting from a dependence of the Angells fragility on the Poisson ratio [V. N. Novikov and A. P. Sokolov, Nature 431, 961 (2004)], and a dependence of the Poisson ratio on the atomic packing density [G. N. Greaves et al., Nat. Mater. 10, 823 (2011)], we propose that the heterogeneities are predominantly density fluctuations in strong glasses (lower Poisson ratio) and shear elasticity fluctuations in fragile glasses (higher Poisson ratio). Because the excess of low-frequency vibration modes in comparison with the Debye regime (boson peak) is strongly connected to these fluctuations, we propose that they are breathing-like (with change of volume) in strong glasses and shear-like (without change of volume) in fragile glasses. As a verification, it is confirmed that the excess modes in the strong silica glass are predominantly breathing-like. Moreover, it is shown that the excess breathing-like modes in a strong polymeric glass are replaced by shear-like modes under hydrostatic pressure as the glass becomes more compact.