Register a new userModulation doping to control the high-density electron gas at a polar/non-polar oxide interface
124
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
A modulation-doping approach to control the carrier density of the high-density electron gas at a prototype polar/non-polar oxide interface is presented. It is shown that the carrier density of the electron gas at a GdTiO3/SrTiO3 interface can be reduced by up to 20% from its maximum value (~ 3x10^14 cm^-2) by alloying the GdTiO3 layer with Sr. The Seebeck coefficient of the two-dimensional electron gas increases concurrently with the decrease in its carrier density. The experimental results provide insight into the origin of charge carriers at oxide interfaces exhibiting a polar discontinuity.
rate research
Read More
The predictions of the polar catastrophe scenario to explain the occurrence of a metallic interface in heterostructures of the solid solution(LaAlO$_3$)$_{x}$(SrTiO$_3$)$_{1-x}$ (LASTO:x) grown on (001) SrTiO$_3$ were investigated as a function of film thickness and $x$. The films are insulating for the thinnest layers, but above a critical thickness, $t_c$, the interface exhibits a constant finite conductivity which depends in a predictable manner on $x$. It is shown that $t_c$ scales with the strength of the built-in electric field of the polar material, and is immediately understandable in terms of an electronic reconstruction at the nonpolar-polar interface. These results thus conclusively identify the polar-catastrophe model as the intrinsic origin of the doping at this polar oxide interface.
Ferroic domain walls could play an important role in microelectronics, given their nanometric size and often distinct functional properties. Until now, devices and device concepts were mostly based on mobile domain walls in ferromagnetic and ferroelectric materials. A less explored path is to make use of polar domain walls in nonpolar ferroelastic materials. Indeed, while the polar character of ferroelastic domain walls has been demonstrated, polarization control has been elusive. Here, we report evidence for the electrostatic signature of the domain-wall polarization in nonpolar calcium titanate (CaTiO3). Macroscopic mechanical resonances excited by an ac electric field are observed as a signature of a piezoelectric response caused by polar walls. On the microscopic scale, the polarization in domain walls modifies the local surface potential of the sample. Through imaging of surface potential variations, we show that the potential at the domain wall can be controlled by electron injection. This could enable devices based on nondestructive information readout of surface potential.
Perovskite oxide heteroepitaxy receives much attention because of the possibility to com- bine the diverse functionalities of perovskite oxide building blocks. A general boundary con- dition for the epitaxy is the presence of polar discontinuities at heterointerfaces. These polar discontinuities result in reconstructions, often creating new functionalities at the interface. However, for a significant number of materials these reconstructions are unwanted as they alter the intrinsic materials properties at the interface. Therefore, a strategy to eliminate this reconstruction of the polar discontinuity at the interfaces is required. We show that the use of compositional interface engineering can prevent the reconstruction at the La0.67Sr0.33MnO3/SrTiO3 (LSMO/STO) interface. The polar discontinuity at this interface can be removed by the insertion of a single La0.33Sr0.67O layer, resulting in improved interface magnetization and electrical conductivity.
The discovery of two-dimensional electron gases (2DEGs) at the heterointerface between two insulating perovskite-type oxides, such as LaAlO3 and SrTiO3, provides opportunities for a new generation of all-oxide electronic and photonic devices. However, significant improvement of the interfacial electron mobility beyond the current value of approximately 1,000 cm2V-1s-1 (at low temperatures), remains a key challenge for fundamental as well as applied research of complex oxides. Here, we present a new type of 2DEG created at the heterointerface between SrTiO3 and a spinel {gamma}-Al2O3 epitaxial film with excellent quality and compatible oxygen ions sublattices. This spinel/perovskite oxide heterointerface exhibits electron mobilities more than one order of magnitude higher than those of perovskite/perovskite oxide interfaces, and demonstrates unambiguous two-dimensional conduction character as revealed by the observation of quantum magnetoresistance oscillations. Furthermore, we find that the spinel/perovskite 2DEG results from interface-stabilized oxygen vacancies and is confined within a layer of 0.9 nm in proximity to the heterointerface. Our findings pave the way for studies of mesoscopic physics with complex oxides and design of high-mobility all-oxide electronic devices.
Atomically flat interfaces between ternary oxides have chemically different variants, depending on the terminating lattice planes of both oxides. Electronic properties change with the interface termination which affects, for instance, charge accumulation and magnetic interactions at the interface. Well-defined terminations have yet rarely been achieved for oxides of ABO3 type (with metals A, B). Here, we report on a strategy of thin film growth and interface characterization applied to fabricate the La0.7Sr0.3MnO3-SrRuO3 interface with controlled termination. Ultra-strong antiferromagnetic coupling between the ferromagnets occurs at the MnO2-SrO interface, but not for the other termination, in agreement with density functional calculations. X-ray magnetic circular dichroism measurements reveal coupled reversal of Mn and Ru magnetic moments at the MnO2-SrO interface. Our results demonstrate termination control of magnetic coupling across a complex oxide interface and provide a pathway for theoretical and experimental explorations of novel electronic interface states with engineered magnetic properties.