Photon correlation spectroscopy and rheological measurements are performed to investigate the microscopic dynamics and mechanical responses of aqueous solutions of triblock copolymers and aqueous mixtures of triblock copolymers and anionic surfactants. Increasing the concentration of triblock copolymers results in a sharp increase in the magnitude of the complex moduli characterising the samples. This is understood in terms of the changes in the aggregation and packing behaviours of the copolymers and the constraints imposed upon their dynamics due to increased close packing. The addition of suitable quantities of an anionic surfactant to a strongly elastic copolymer solution results in a decrease in the complex moduli of the samples by several decades. It is argued that the shape anisotropy and size polydispersity of the micelles comprising mixtures cause dramatic changes in the packing behaviour, resulting in sample unjamming and the observed decrease in complex moduli. Finally, a phase diagram is constructed in the temperature-surfactant concentration plane to summarise the jamming-unjamming behaviour of aggregates constituting triblock copolymer-anionic surfactant mixtures.
rate research
Read More
Synperonic F-108 (generic name, pluronic) is a micelle forming triblock copolymer of type ABA, where A is polyethylene oxide (PEO) and B is polypropylene oxide (PPO). At high temperatures, the hydrophobicity of the PPO chains increase, and the pluronic molecules, when dissolved in an aqueous medium, self-associate into spherical micelles with dense PPO cores and hydrated PEO coronas. At appropriately high concentrations, these micelles arrange in a face centred cubic lattice to show inverse crystallization, with the samples exhibiting high-temperature crystalline and low-temperature fluidlike phases. By studying the evolution of the elastic and viscous moduli as temperature is increased at a fixed rate, we construct the concentration-temperature phase diagram of Synperonic F-108. For a certain range of temperatures and at appropriate sample concentrations, we observe a predominantly elastic response. Oscillatory strain amplitude sweep measurements on these samples show pronounced peaks in the loss moduli, a typical feature of soft solids. The soft solid-like nature of these materials is further demonstrated by measuring their frequency dependent mechanical moduli. The storage moduli are significantly larger than the loss moduli and are almost independent of the applied angular frequency. Finally, we perform strain rate frequency superposition (SRFS) experiments to measure the slow relaxation dynamics of this soft solid.
We have used the Scheutjens-Fleer self-consistent field (SF-SCF) method to predict the self-assembly of triblock copolymers with a solvophilic middle block and sufficiently long solvophobic outer blocks. We model copolymers consisting of polyethylene oxide (PEO) as solvophilic block and poly(lactic-co-glycolic) acid (PLGA) or poly({ko}-caprolactone) (PCL) as solvophobic block. These copolymers form structurally quenched spherical micelles provided the solvophilic block is long enough. Predictions are calibrated on experimental data for micelles composed of PCL-PEO-PCL and PLGA-PEO-PLGA triblock copolymers prepared via the nanoprecipitation method. We establish effective interaction parameters that enable us to predict various micelle properties such as the hydrodynamic size, the aggregation number and the loading capacity of the micelles for hydrophobic species that are consistent with experimental finding.
We examined the kinetics of the transformation from the lamellar (LAM) to the hexagonally packed cylinder (HEX) phase for the triblock copolymer, polystyrene-b-poly (ethylene-co-butylene)-b-polystyrene (SEBS) in dibutyl phthalate (DBP), a selective solvent for polystyrene (PS), using time-resolved small angle x-ray scattering (SAXS). We observe the HEX phase with the EB block in the cores at a lower temperature than the LAM phase due to the solvent selectivity of DBP for the PS block. Analysis of the SAXS data for a deep temperature quench well below the LAM-HEX transition shows that the transformation occurs in a one-step process. We calculate the scattering using a geometric model of rippled layers with adjacent layers totally out of phase during the transformation. The agreement of the calculations with the data further supports the continuous transformation mechanism from the LAM to HEX for a deep quench. In contrast, for a shallow quench close to the OOT we find agreement with a two-step nucleation and growth mechanism.
Time-resolved small angle x-ray scattering (SAXS) was used to examine the kinetics of the transition from HEX cylinders to BCC spheres at various temperatures in poly(styrene-b- ethylene-co-butylene-b-styrene) (SEBS) in mineral oil, a selective solvent for the middle EB block. Temperature-ramp SAXS and rheology measurements show the HEX to BCC order-order transition (OOT) at ~127 oC and order-disorder transition (ODT) at ~180 oC. We also observed the metastability limit of HEX in BCC with a spinodal temperature, Ts ~ 150 oC. The OOT exhibits 3 stages and occurs via a nucleation and growth mechanism when the final temperature Tf < Ts. Spinodal decomposition in a continuous ordering system was seen when Ts< Tf < TODT. We observed that HEX cylinders transform to disordered spheres via a transient BCC state. We develop a geometrical model of coupled anisotropic fluctuations and calculate the scattering which shows very good agreement with the SAXS data. The splitting of the primary peak into two peaks when the cylinder spacing and modulation wavelength are incommensurate predicted by the model is confirmed by analysis of the SAXS data.
The kinetics of the transformation from the hexagonal packed cylinder (HEX) phase to the face-centered-cubic (FCC) phase was simulated using Brownian Dynamics for an ABA triblock copolymer in a selective solvent for the A block. The kinetics was obtained by instantaneously changing either the temperature of the system or the well-depth of the Lennard-Jones potential. Detailed analysis showed that the transformation occurred via a rippling mechanism. The simulation results indicated that the order-order transformation (OOT) was a nucleation and growth process when the temperature of the system instantly jumped from 0.8 to 0.5. The time evolution of the structure factor obtained by Fourier Transformation showed that the peak intensities of the HEX and FCC phases could be fit well by an Avrami equation.