Two B-site ordered double perovskites, La2LiMoO6 and Ba2YMoO6, based on the S = 1/2 ion, Mo5+, have been investigated in the context of geometric magnetic frustration. Powder neutron diffraction, heat capacity, susceptibility, muon spin relaxation(_SR), and 89Y NMR- including MAS NMR- data have been collected. La2LiMoO6 deviates strongly from simple Curie-Weiss paramagnetic behavior below 150K and zero-field cooled/ field cooled (ZFC/FC)irreversibility occurs below 20K with a weak, broad susceptibility maximum near 5K in the ZFC data. A Curie-Weiss fit shows a reduced mu_eff=1.42mu_B, (spin only = 1.73 muB) and a Weiss temperature, theta_c, which depends strongly on the temperature range of the fit. Powder neutron diffraction, heat capacity and 7Li NMR show no evidence for long range magnetic order to 2K. On the other hand oscillations develop below 20K in muSR indicating at least short range magnetic correlations. Susceptibility data for Ba2YMoO6 also deviate strongly from the C-W law below 150K with a similarly reduced mu_eff = 1.72mu_B and theta_c = - 219(1)K. Heat capacity, neutron powder diffraction and muSR data show no evidence for long range order to 2K but a very broad maximum appears in the heat capacity. The 89Y NMR paramagnetic Knight shift shows a remarkable local spin susceptibility behavior below about 70K with two components from roughly equal sample volumes, one indicating a singlet state and the other a strongly fluctuating paramagnetic state. Further evidence for a singlet state comes from the behavior of the relaxation rate, 1/T1. These results are discussed and compared with those from other isostructural S = 1/2 materials and those based on S = 3/2 and S = 1.
Download