We report synthesis, structural details and magnetization of SmFe1-xCoxAsO with x ranging from 0.0 to 0.30. It is found that Co substitutes fully at Fe site in SmFeAsO in an iso-structural lattice with slightly compressed cell. The parent compound exhibited known spin density wave (SDW) character below at around 140 K. Successive doping of Co at Fe site suppressed the SDW transition for x = 0.05 and later induced superconductivity for x = 0.10, 0.15 and 0.20 respectively at 14, 15.5 and 9K. The lower critical field as seen from magnetization measurements is below 200Oe. The appearance of bulk superconductivity is established by wide open isothermal magnetization M(H) loops. Superconductivity is not observed for higher content of Co i.e. x = 0.30. Clearly the Co substitution at Fe site in SmFe1-xCoxAsO diminishes the Fe SDW character, introduces bulk superconductivity for x between 0.10 and 0.20 and finally becomes non-superconducting for x above 0.20. The Fe2+ site Co3+ substitution injects mobile electrons to the system and superconductivity appears, however direct substitution introduces simultaneous disorder in superconducting FeAs layer and thus superconductivity disappears for higher content of Co.
rate research
Read More
We report the synthesis and physical property characterization of PrFe1-xCoxAsO with x = 0.0 to 1.0. The studied samples are synthesized by solid state reaction route via vacuum encapsulation method. The pristine compound PrFeAsO does not show superconductivity, but rather exhibits a metallic step like transition due to spin density wave ordering of Fe moments below 150 K, followed by another upward step due to anomalous ordering of Pr moments at 12 K. Both the Fe-SDW and Pr-TN temperatures decrease monotonically with Co substitution at Fe site. Superconductivity appears in a narrow range of x from 0.07 to 0.25 with maximum Tc at 11.12 K for x = 0.15. Samples, with x = 0.25 exhibit metallic behavior right from 300 K down to 2 K, without any Fe-SDW or Pr-TN steps in resistivity. In fact, though Fe-SDW decreases monotonically, the Pr-TN is disappeared even with x = 0.02. The magneto transport measurements below 14 Tesla on superconducting polycrystalline Co doped PrFeAsO lead to extrapolated values of the upper critical fields [Hc2(0)] of up to 60 Tesla.
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l) plane i.e., orientation in c-direction. All the crystals possess tetragonal structure having P4/nmm space group. Detailed scanning electron microscopy (SEM) images show that the crystals are grown in slab-like morphology. The EDAX results revealed the final elemental composition to be near stoichiometric. Powder X-Ray diffraction (PXRD) Rietveld analysis results show that (00l) peaks are shifted towards higher angle with increasing Co concentration. Both a and c lattice parameters decrease with increasing Co concentration in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals. Low temperature transport and magnetic measurements show that the superconducting transition temperature (Tc), decreases from around 12K to 10K and 4K for x=0.03 and x=0.05 respectively. For x=0.10 crystal superconductivity is not observed down to 2K.
We report the experimental results of temperature dependent polarized As K-edge extended x-ray absorption fine structure (EXAFS) of LaFe1-xCoxAsO (x=0.0 and 0.11) single-crystals. By aligning the Fe-As bond direction in the direction of the x-ray beam polarization we have been able to identify an anomaly in the Fe-As bond correlations at the tetragonal to orthorhombic transition at 150K, while previous investigations with standard unpolarized EXAFS of undoped LaFeAsO powder samples were not able to detect any such anomaly. Using our approach we have been able to identify in the superconducting doped sample, LaFe0.89Co0.11AsO, a broad anomaly around 60 K. The low temperature anomaly has good correlations with the temperature dependence of several properties like resistivity, magnetic susceptibility, linear thermal expansion, etc indicating the emergence of the dynamical oscillations of the Fe - As pairs
The phase diagram of NdFe1-xCoxAsO for low cobalt substitution consists of a superconducting dome (0.05 < x < 0.20) with a maximum critical temperature of 16.5(2) K for x = 0.12. The x = 1 end member, NdCoAsO, is an itinerant ferromagnet (TC = 85 K) with an ordered moment of 0.30(1) BM at 15 K. Below TN = 9 K, Nd spin-ordering results in the antiferromagnetic coupling of the existing ferromagnetic planes. Rietveld analysis reveals that the electronically important two-fold tetrahedral angle increases from 111.4 to 115.9 deg. in this series. Underdoped samples with x = 0.046(2) and x = 0.065(2) show distortions to the orthorhombic Cmma structure at 72(2) and 64(2) K, respectively. The temperature dependences of the critical fields Hc2(T) near Tc are linear with almost identical slopes of 2.3(1) T K-1 for x = 0.065(2), x = 0.118(2) and x = 0.172(2). The estimated critical field Hc2(0) and correlation length for optimally doped samples are 26(1) T and 36(1) Angstrom. A comparison of the maximum reported critical temperatures of well-characterized cobalt doped 122- and 1111-type superconductors is presented.
Superconductivity and ferromagnetism are two antagonistic cooperative phenomena, which makes it difficult for them to coexist. Here we demonstrate experimentally that they do coexist in EuFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$ with $0.2leq xleq0.4$, in which superconductivity is associated with Fe-3$d$ electrons and ferromagnetism comes from the long-range ordering of Eu-4$f$ moments via Ruderman-Kittel-Kasuya-Yosida (RKKY) interactions. The coexistence is featured by large saturated ferromagnetic moments, high and comparable superconducting and magnetic transition temperatures, and broad coexistence ranges in temperature and field. We ascribe this unusual phenomenon to the robustness of superconductivity as well as the multi-orbital characters of iron pnictides.