Register a new userSynthesis and Physical Properties of FeSe1/2Te1/2 Superconductor
211
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
One of the most important properties of very recently reported FeSe based superconductors is the robustness of their superconductivity under applied magnetic field. The synthesis and control of superconductivity in FeSe based compounds is rather a difficult task. Synthesis and physical property characterization for optimized superconductivity of FeSe1/2Te1/2 at 13 K is reported here. The compound crystallized in a tetragonal structure with lattice parameters a = 3.8008(10) and c = 6.0187 (15) A. Magnetization measurements indicated bulk superconductivity with lower critical field (Hc1) of around 180 Oe. By applying Ginzburg Landau (GL) theory, the Hc2(0) value is estimated to be = 1840 kOe for the 90% of resistive transition. A heat capacity measurement revealed bulk superconductivity by a hump at Tc near 13 K, and an expected decrease was observed under an applied magnetic field.
rate research
Read More
The bulk polycrystalline sample FeSe1/2Te1/2 is synthesized by solid state reaction route in an evacuated sealed quartz tube at 750 oC. The presence of superconductivity is confirmed through magnetization/thermoelectric/resistivity studies. It is found that the superconducting transition temperature (Tc) is around 12 K. Heat capacity (Cp) of superconducting FeSe1-xTex exhibited a hump near Tc, instead of well defined Lambda transition. X-ray Photo electron spectroscopy (XPS) studies revealed well defined positions for divalent Fe, Se and Te but with sufficient hybridization of Fe (2p) and Se/Te (3d) core levels. In particular divalent Fe is shifted to higher BE (binding energy) and Se and Te to lower. The situation is similar to that as observed earlier for famous Cu based HTSc (High Tc superconductors), where Cu (3d) orbital hybridizes with O (2p). We also found the satellite peak of Fe at 712.00 eV, which is attributed to charge carrier localization induced by Fe at 2c site.
Transition metal boride Ru$_7$B$_3$ was found to be a noncentrosymmetric superconductor with $T_{C}$ equal to 3.3 K. Superconducting and normal state properties of Ru$_7$B$_3$ were determined by a self-consistent analysis through resistivity($rho_{xx}$ and $rho_{xy}$), specific heat, lower critical field measurement and electronic band structure calculation. It is found that Ru$_7$B$_3$ belongs to an s-wave dominated single band superconductor with energy gap 0.5 meV and could be categorized into type II superconductor with weak electron-phonon coupling. Unusual kink feature is clearly observed in field-broadening resistivity curves, suggesting the possible mixture of spin triplet induced by the lattice without inversion symmetry.
In this article we review our studies of the K0.80Fe1.76Se2 superconductor, with an attempt to elucidate the crystal growth details and basic physical properties over a wide range of temperatures and applied magnetic field, including anisotropic magnetic and electrical transport properties, thermodynamic, London penetration depth, magneto-optical imaging and Mossbauer measurements. We find that: (i) Single crystals of similar stoichiometry can be grown both by furnace-cooled and decanted methods; (ii) Single crystalline K0.80Fe1.76Se2 shows moderate anisotropy in both magnetic susceptibility and electrical resistivity and a small modulation of stoichiometry of the crystal, which gives rise to broadened transitions; (iii) The upper critical field, Hc2(T) is ~ 55 T at 2 K for H||c, manifesting a temperature dependent anisotropy that peaks near 3.6 at 27 K and drops to 2.5 by 18 K; (iv) Mossbauer measurements reveal that the iron sublattice in K0.80Fe1.76Se2 clearly exhibits magnetic order, probably of the first order, from well below Tc to its Neel temperature of Tn = 532 +/- 2 K. It is very important to note that, although, at first glance there is an apparent dilemma posed by these data: high Tc superconductivity in a near insulating, large ordered moment material, analysis indicates that the sample may well consist of two phases with the minority superconducting phase (that does not exhibit magnetic order) being finely distributed, but connected with in an antiferromagnetic, poorly conducting, matrix, essentially making a superconducting aerogel.
We report successful growth of flux free large single crystals of superconducting FeSe1/2Te1/2 with typical dimensions of up to few cm. The AC and DC magnetic measurements revealed the superconducting transition temperature (Tc) value of around 11.5K and the iso-thermal MH showed typical type-II superconducting behavior. The lower critical field being estimated by measuring the low field iso-thermal magnetization in superconducting regime is found to be above 200 Oe at 0K.
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples of MgB2, processed under identical conditions. The compound crystallizes in hexagonal structure with space group P6/mmm. Transmission electron microscopy (TEM) reveals electron micrographs showing various types of defect features along with the presence of 3-4nm thick amorphous layers forming the grain boundaries of otherwise crystalline MgB2. Raman spectra of the compound at room temperature exhibited characteristic phonon peak at 600 cm-1. Superconductivity is observed at 37.2K by magnetic susceptibility C(T), resistivity R(T), thermoelectric power S(T), and thermal conductivity K(T) measurements. The power law fitting of R(T) give rise to Debye temperature at 1400K which is found consistent with the theoretical fitting of S(T), exhibiting ThetaD of 1410K and carrier density of 3.81x 1028/m3. Thermal conductivity K(T) shows a jump at 38K, i.e., at Tc, which was missing in some earlier reports. Critical current density (Jc) of up to 105 A/cm2 in 1-2T (Tesla) fields at temperatures (T) of up to 10K is seen from magnetization measurements. The irreversibility field, defined as the field related to merging of M(H) loops is found to be 78, 68 and 42 kOe at 4, 10 and 20K respectively. The superconducting performance parameters viz. irreversibility field (Hirr) and critical current density Jc(H) of the studied MgB2 are improved profoundly with addition of nano-SiC and nano-Diamond. The physical property parameters measured for polycrystalline MgB2 are compared with earlier reports and a consolidated insight of various physical properties is presented.