Register a new userObservation of quantum-Hall effect in gated epitaxial graphene grown on SiC (0001)
193
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Epitaxial graphene films were formed on the Si-face of semi-insulating 4H-SiC substrates by a high temperature sublimation process. A high-k gate stack on epitaxial graphene is realized by inserting a fully oxidized nanometer thin aluminum film as a seeding layer followed by an atomic-layer deposition process. The electrical properties of epitaxial graphene films are sustained after gate stack formation without significant degradation. At low temperatures, the quantum-Hall effect in Hall resistance is observed along with pronounced Shubnikov-de Hass oscillations in diagonal magneto-resistance of gated epitaxial graphene on SiC (0001).
rate research
Read More
In this letter we report on transport measurements of epitaxial graphene on SiC(0001) with oxygen adsorption. In a $50times 50 mumathrm{m^2}$ size Hall bar we observe the half-integer quantum Hall effect with a transverse resistance plateau quantized at filling factor around $ u = 2$, an evidence of monolayer graphene. We find low electron concentration of $9times 10^{11} textrm{cm}^{-2}$ and we show that a doping of $10^{13}textrm{cm}^{-2}$ which is characteristic of intrinsic epitaxial graphene can be restored by vacuum annealing. The effect of oxygen adsorption on carrier density is confirmed by local angle-resolved photoemission spectroscopy measurements. These results are important for understanding oxygen adsorption on epitaxial graphene and for its application to metrology and mesoscopic physics where a low carrier concentration is required.
We present electronic structure calculations of few-layer epitaxial graphene nanoribbons on SiC(0001). Trough an atomistic description of the graphene layers and the substrate within the extended H{u}ckel Theory and real/momentum space projections we argue that the role of the heterostructures interface becomes crucial for the conducting capacity of the studied systems. The key issue arising from this interaction is a Fermi level pinning effect introduced by dangling interface bonds. Such phenomenon is independent from the width of the considered nanostructures, compromising the importance of confinement in these systems.
We present a structural analysis of the graphene-4HSiC(0001) interface using surface x-ray reflectivity. We find that the interface is composed of an extended reconstruction of two SiC bilayers. The interface directly below the first graphene sheet is an extended layer that is more than twice the thickness of a bulk SiC bilayer (~1.7A compared to 0.63A). The distance from this interface layer to the first graphene sheet is much smaller than the graphite interlayer spacing but larger than the same distance measured for graphene grown on the (000-1) surface, as predicted previously by ab intio calculations.
Interest in the use of graphene in electronic devices has motivated an explosion in the study of this remarkable material. The simple, linear Dirac cone band structure offers a unique possibility to investigate its finer details by angle-resolved photoelectron spectroscopy (ARPES). Indeed, ARPES has been performed on graphene grown on metal substrates but electronic applications require an insulating substrate. Epitaxial graphene grown by the thermal decomposition of silicon carbide (SiC) is an ideal candidate for this due to the large scale, uniform graphene layers produced. The experimental spectral function of epitaxial graphene on SiC has been extensively studied. However, until now the cause of an anisotropy in the spectral width of the Fermi surface has not been determined. In the current work we show, by comparison of the spectral function to a semi-empirical model, that the anisotropy is due to small scale rotational disorder ($simpm$ 0.15$^{circ}$) of graphene domains in graphene grown on SiC(0001) samples. In addition to the direct benefit in the understanding of graphenes electronic structure this work suggests a mechanism to explain similar variations in related ARPES data.
The observation of the anomalous quantum Hall effect in exfoliated graphene flakes triggered an explosion of interest in graphene. It was however not observed in high quality epitaxial graphene multilayers grown on silicon carbide substrates. The quantum Hall effect is shown on epitaxial graphene monolayers that were deliberately grown over substrate steps and subjected to harsh processing procedures, demonstrating the robustness of the epitaxial graphene monolayers and the immunity of their transport properties to temperature, contamination and substrate imperfections. The mobility of the monolayer C-face sample is 19,000 cm^2/Vs. This is an important step towards the realization of epitaxial graphene based electronics.