We study the low-temperature magneto-photoluminescence (PL) from individual CdSe nanocrystals. Nanocrystals having a small bright exciton fine structure splitting ($<$0.5 meV) exhibit a conventional left- and right-circularly polarized Zeeman PL doublet in applied magnetic fields. In contrast, nanocrystals with large fine structure splitting ($>$1 meV) show an anomalous magneto-PL polarization, wherein the lower-energy peak becomes circularly polarized with increasing field, while the higher-energy peak remains linearly polarized. This unusual behavior arises from strong mixing between the absorbing and emitting bright exciton levels due to strong anisotropic exchange interactions.
We report the direct observation of the spin-singlet dark excitonic state in individual single-walled carbon nanotubes through low-temperature micro-photoluminescence spectroscopy in magnetic fields. A magnetic field up to 5 T, applied along the nanotube axis, brightened the dark state, leading to the emergence of a new emission peak. The peak rapidly grew in intensity with increasing field at the expense of the originally-dominant bright exciton peak and finally became dominant at fields $>$3 T. This behavior, universally observed for more than 50 nanotubes of different chiralities, can be quantitatively explained through a model incorporating the Aharonov-Bohm effect and intervalley Coulomb mixing, unambiguously proving the existence of dark excitons. The directly measured dark-bright splitting values were 1-4 meV for tube diameters 1.0-1.3 nm. Scatter in the splitting value emphasizes the role of the local environment surrounding a nanotube in determining the excitonic fine structure of single-walled carbon nanotubes.