We report on the inelastic-scattering rate of electrons on phonons and relaxation of electron energy studied by means of magnetoconductance, and photoresponse, respectively, in a series of strongly disordered superconducting NbN films. The studied films with thicknesses in the range from 3 to 33 nm are characterized by different Ioffe-Regel parameters but an almost constant product q_Tl(q_T is the wave vector of thermal phonons and l is the elastic mean free path of electrons). In the temperature range 14-30 K, the electron-phonon scattering rates obey temperature dependencies close to the power law 1/tau_{e-ph} sim T^n with the exponents n = 3.2-3.8. We found that in this temperature range tau_{e-ph} and n of studied films vary weakly with the thickness and square resistance. At 10 K electron-phonon scattering times are in the range 11.9-17.5 ps. The data extracted from magnetoconductance measurements were used to describe the experimental photoresponse with the two-temperature model. For thick films, the photoresponse is reasonably well described without fitting parameters, however, for thinner films, the fit requires a smaller heat capacity of phonons. We attribute this finding to the reduced density of phonon states in thin films at low temperatures. We also show that the estimated Debye temperature in the studied NbN films is noticeably smaller than in bulk material.
قيم البحث
اقرأ أيضاً
We report on the direct measurement of the electron-phonon relaxation time, {tau}eph, in disordered TiN films. Measured values of {tau}eph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T-3 temperature dependence
. The electronic density of states at the Fermi level N0 is estimated from measured material parameters. The presented results confirm that thin TiN films are promising candidate-materials for ultrasensitive superconducting detectors.
The suppression of superconductivity in disordered systems is a fundamental problem of condensed matter physics. Here we investigate the superconducting niobium-titanium-nitride (Nb_{1-x}Ti_{x}N) thin films grown by atomic layer deposition (ALD) wher
e disorder is controlled by the slight tuning of the ALD process parameters. We observe the smooth crossover from the disorder-driven superconductor-normal metal transition (often reffered to as fermionic mechanism) to the case where bosonic mechanism dominates and increasing disorder leads to formation of metal with Cooper pairing. We show that, in moderately disordered films, the transition to zero-resistance state occurs in a full agreement with the conventional theories of superconducting fluctuations and Berezinskii-Kosterlitz-Thouless transition. However, the critically disordered films violate this accord showing low-temperature features possibly indicating the Bose metal phase. We show that it is the interrelation between films sheet resistance in the maximum, R_{max}, of the resistive curve R(T) and R_q = h/4e^2 that distinguishes between these two behaviors. We reveal the characteristic features in magnetoresistance of the critically disordered films with R_{max} > R_q
We present a physically consistent interpretation of the dc electrical properties of niobiumnitride (NbN)-based superconducting hot-electron bolometer (HEB-) mixers, using concepts of nonequilibrium superconductivity. Through this we clarify what phy
sical information can be extracted from the resistive transition and the dc current-voltage characteristics, measured at suitably chosen temperatures, and relevant for device characterization and optimization. We point out that the intrinsic spatial variation of the electronic properties of disordered superconductors, such as NbN, leads to a variation from device to device.
Using scanning tunneling spectroscopy (STS), we address the problem of the superconductor-insulator phase transition (SIT) in homogeneously disordered ultrathin (2-15 nm) films of NbN. Samples thicker than 8 nm, for which the Ioffe-Regel parameter $k
_F l geq 5.6$, manifest a conventional superconductivity : A spatially homogeneous BCS-like gap, vanishing at the critical temperature, and a vortex lattice in magnetic field. Upon thickness reduction, however, while $k_F l$ lowers, the STS revealed striking deviations from the BCS scenario, among which a progressive decrease of the coherence peak height and spatial inhomogeneities. The thinnest film (2.16 nm), while not being exactly at the SIT ($T_C approx 0.4 T_{C-bulk}$), showed astonishingly vanishing coherence peaks and the absence of vortices. In the quasi-2D limit, such clear signatures of the loss of long-range phase coherence strongly suggest that, at the SIT the superconductivity is destroyed by phase fluctuations.
We report a study of the relaxation time of the restoration of the resistive superconducting state in single crystalline boron-doped diamond using amplitude-modulated absorption of (sub-)THz radiation (AMAR). The films grown on an insulating diamond
substrate have a low carrier density of about 2.5x10^{21} cm^{-3} and a critical temperature of about 2 K. By changing the modulation frequency we find a high-frequency rolloff which we associate with the characterstic time of energy relaxation between the electron and the phonon systems or the relaxation time for nonequilibrium superconductivity. Our main result is that the electron-phonon scattering time varies clearly as T^{-2}, over the accessible temperature range of 1.7 to 2.2 K. In addition, we find, upon approaching the critical temperature T_c, evidence for an increasing relaxation time on both sides of T_c.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها