The complexity of the Portevin-Le Chatelier effect in Al-2.5%Mg polycrystalline samples subjected to uniaxial tensile tests is quantified. Multiscale entropy analysis is carried out on the stress time series data observed during jerky flow to quantify the complexity of the distinct spatiotemporal dynamical regimes. It is shown that for the static type C band, the entropy is very low for all the scales compared to the hopping type B and the propagating type A bands. The results are interpreted considering the time and length scales relevant to the effect.
The scaling behavior of the Portevin-Le Chatelier (PLC) effect was studied by deforming Al-2.5%Mg alloy for a wide range of strain rates. To reveal the exact scaling nature, the time series data of true stress vs. time, obtained during deformation, w
Tensile tests were carried out by deforming polycrystalline samples of Al-2.5%Mg alloy at four different temperatures in an intermediate strain rate regime of 2x10-4s-1 to 2x10-3s-1. The Portevin-Le Chatelier (PLC) effect was observed throughout the
The Portevin-Le Chatelier(PLC) effect has been investigated by deforming Al-2.5%Mg alloy in the strain rate regime where simultaneously two types (type B and type A) of serrations appear in the stress strain curve. Our analysis reveal that in this st
The scaling behavior of the Portevin-Le Chatelier (PLC) effect is studied by deforming a substitutional alloy, Al-2.5%Mg and an interstitial alloy, low carbon steel (0.15%C, 0.33%Mn, 0.04%P, 0.05%S, 0.15%Si and rest Iron) at room temperature for a wi
The plastic deformation of dilute alloys is often accompanied by plastic instabilities due to dynamic strain aging and dislocation interaction. The repeated breakaway of dislocations from and their recapture by solute atoms leads to stress serrations