تسجيل مستخدم جديدDomain Matching Epitaxy of Ferroelectric Hf0.5Zr0.5O2(111) on La2/3Sr1/3MnO3(001)
196
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Epitaxial ferroelectric HfO2 films are the most suitable to investigate intrinsic properties of the material and for prototyping emerging devices. Ferroelectric Hf0.5Zr0.5O2(111) films have been epitaxially stabilized on La2/3Sr1/3MnO3(001) electrodes. This epitaxy, considering the symmetry dissimilarity and the huge lattice mismatch, is not compatible with conventional mechanisms of epitaxy. To gain insight into the epitaxy mechanism, scanning transmission electron microscopy characterization of the interface was performed, revealing arrays of dislocations with short periodicities. These observed periodicities agree with the expected for domain matching epitaxy, indicating that this unconventional mechanism could be the prevailing factor in the stabilization of ferroelectric Hf0.5Zr0.5O2 with (111) orientation in the epitaxial Hf0.5Zr0.5O2(111)/La2/3Sr1/3MnO3(001) heterostructure.
قيم البحث
اقرأ أيضاً
Understanding and manipulating properties emerging at a surface or an interface require a thorough knowledge of structure-property relationships. We report a study of a prototype oxide system, La2/3Sr1/3MnO3 grown on SrTiO3(001), by combining in-situ
angle-resolved x-ray photoelectron spectroscopy, ex-situ x-ray diffraction, and scanning transmission electron microscopy/spectroscopy with electric transport measurements. We find that La2/3Sr1/3MnO3 films thicker than 20 unit cells (u.c.) exhibit a universal behavior with no more than one u.c. intermixing at the interface but at least 3 u.c. of Sr segregation near the surface which is (La/Sr)O terminated. The conductivity vs film thickness shows the existence of nonmetallic layers with thickness ~ 6.5 +/- 0.9 u.c., which is independent of film thickness but mainly relates to the deviation of Sr concentration near the surface region. Below 20 u.c., the surface of the films appears mixed (La/Sr)O with MnO2 termination. Decreasing film thickness to less than 10 u.c. leads to the enhanced deviation of chemical composition in the films and eventually drives the film insulating. Our observation offers a natural explanation for the thickness-driven metal-nonmetal transition in thin films based on the variation of film stoichiometry.
The electronic structure and equilibrium geometry of La2/3Sr1/3MnO3 are studied theoretically by means of density functional calculations. The doping is treated by introducing holes and a compensating jellium background. The results for the local den
sity approximation (LDA) agree with previous LDA calculations, with an equilibrium volume 5.3% too small and with both majority and minority spin states present at the Fermi level for the relaxed system. The generalised gradient approximation (GGA) offers a qualitatively improved description of the system, with a more realistic volume, and a half-metallic behaviour for the relaxed structure, which enables studies needing theoretical relaxation.The ideal MnO2-terminated (001) surface is then described with explicit doping.
We analyze X-ray diffraction data used to extract cell parameters of ultrathin films on closely matching substrates. We focus on epitaxial La2/3Sr1/3MnO3 films grown on (001) SrTiO3 single crystalline substrates. It will be shown that, due to extreme
ly high structural similarity of film and substrate, data analysis must explicitly consider the distinct phase of the diffracted waves by substrate and films to extract reliable unit cell parameters. The implications of this finding for the understanding of strain effects in ultrathin films and interfaces will be underlined
We studied ZrO2-La2/3Sr1/3MnO3 pillar matrix thin films which were found to show anomalous magnetic and electron transport properties controlled by the amount of ZrO2. With the application of an aberration corrected transmission electron microscope,
structure and chemical information of the system, especially of the pillar matrix interface were revealed at atomic resolution. Minor amounts of Zr were found to occupy Mn positions within the matrix and its solubility within the matrix was found to be less than 6 mol%. Moreover, the Zr concentration reached minimum concentration at the pillar matrix interface accompanied by oxygen deficiency. La and Mn diffusion into the pillar was observed along with a change of the Mn valence state. La and Mn positions inside ZrO2 pillars were also revealed at atomic resolution. These results provide detailed information for future studies of macroscopic properties of these materials.
The magnetic properties of a series of YBa2Cu3O7-x/La2/3Ca1/3MnO3 (YBCO/LC1/3MO) superlattices grown by dc sputtering at high oxygen pressures (3.5 mbar) show the expected ferromagnetic behaviour. However, field cooled hysteresis loops at low tempera
ture show the unexpected existence of exchange bias, effect associated with the existence of ferromagnetic/antiferromagnetic (F/AF) interfaces. The blocking temperature (TB) is found thickness dependent and the exchange bias field (HEB) is found inversely proportional to the FM layer thickness, as expected. The presence of an AF material is probably associated to interface disorder and Mn valence shift towards Mn4+.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها