تسجيل مستخدم جديدBlack and White Anatase, Rutile and Mixed Forms: Band-Edges and Photocatalytic Activity
51
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Here we investigate the band-level energetics of black hydrogenated titania in different polymorphs using in-situ photoelectrochemical measurements and XPS valence band measurements. We find that the conduction band of black rutile is higher in energy than in black anatase by 0.4 eV. For photocatalytic hydrogen generation, in a polymorph hetero-junction such as in black Degussa P25, thus black rutile can act as a photosensitizer while black anatase provides charge-mediation catalysis onto H2O to generate H2. By optimizing the thermal reduction conditions of black anatase/rutile junctions the H2 production can be significantly increased.
قيم البحث
اقرأ أيضاً
Black TiO2 has gained increasing interest because of its outstanding properties and promising applications in a wide range of fields. Among the outstanding features of the material is that certain synthesis processes lead to the formation of an intri
nsic co-catalytic center and thus enable noble-metal free photocatalytic H2 generation. In this work, we report grey TiO2 by an appropriate hydrogenation treatment exhibits excellent photocatalytic hydrogen. In this case, by the employment of thermally stable and high-surface-area TiO2 nanoparticles as well as mesoporous particles as the hydrogenation precursor, the appropriate extent of reduction of TiO2 (coloration) and the formation of Ti3+ is the key for the efficient noble-metal-free photocatalytic H2 generation. The EPR results reveal that grey TiO2 shows stronger Ti3+ feature at g ca. 1.93 than black TiO2 contributing to the intrinsic catalytic center for H2 evolution.
In this work, we demonstrate that a well-established and facile ball milling approach using mixtures of commercial anatase nanoparticles and TiH2 introduces noble-metal-free photocatalytic H2 activity to titania. We characterize this synergistic effe
ct in view of the nature of defects, state of hydroxylation, and investigate the effect on the energetics and kinetics of electronic states and the resulting H2 evolution performance.
Gold-decorated TiO$_2$ nanotubes were used for the photocatalytic abatement of Hg(II) in aqueous solutions. The presence of dewetted Au nanoparticles induces a strong enhancement of photocatalytic reduction and scavenging performances, with respect t
o naked TiO$_2$. In the presence of chlorides, a massive formation of Hg2Cl2 nanowires, produced from Au nanoparticles, was observed using highly Au loaded photocatalysts to treat a 10 ppm Hg(II) solution. EDS and XPS confirmed the nature of the photo-produced nanowires. In the absence of chlorides and/or at lower Hg(II) starting concentrations, the scavenging of mercury proceeds through the formation of Hg-Au amalgams. Solar light driven Hg(II) abatements up to 90% were observed after 24h. ICP-MS analysis revealed that the removed Hg(II) is accumulated on the photocatalyst surface. Regeneration of Hg-loaded exhaust photocatalysts was easily performed by anodic stripping of Hg(0) and Hg(I) to Hg(II). After four catalytic-regeneration cycles only a 10% decrease of activity was observed.
We investigate the photocatalytic performance of nanocomposites prepared in a one-step process by liquid-phase exfoliation of graphite in the presence of TiO$_2$ nanoparticles (NPs) at atmospheric pressure and in water, without heating or adding any
surfactant, and starting from low-cost commercial reagents. The nanocomposites show enhanced photocatalytic activity, degrading up to 40$%$ more pollutants with respect to the starting TiO$_2$-NPs. In order to understand the photo-physical mechanisms underlying this enhancement, we investigate the photo-generation of reactive species (trapped holes and electrons) by ultrafast transient absorption spectroscopy. We observe an electron transfer process from TiO$_2$ to the graphite flakes within the first picoseconds of the relaxation dynamics, which causes the decrease of the charge recombination rate, and increases the efficiency of the reactive species photo-production.
We present theoretical evidence for local magnetic moments on Ti3+ ions in oxygen-deficient anatase and rutile TiO2 observed in a recent experiment [S. Zhou, et al., Phys. Rev. B 79, 113201 (2009)]. Results of our first-principles GGA+U calculations
reveal that an oxygen vacancy converts two Ti4+ ions to two Ti3+ ions in anatase phase, which results in a local magnetic moment of 1.0 $mu_B$ per Ti3+. The two Ti3+ ions, however, form a stable antiferromagnetic state, and similar antiferromagnetism is also observed in oxygen-deficient rutile phase TiO2. The calculated results are in good agreement with the experimentally observed antiferromagnetic-like behavior in oxygen-deficient Ti-O systems.