Large single crystals of the double-perovskite Ba$_2$ScNbO$_6$ were grown from the melt for the first time. With a lattice parameter at room temperature of 4.11672(1) r{A}, this cubic double-perovskite has an excellent lattice match to BaSnO$_3$, PbZr$_{0.9}$Ti$_{0.1}$O$_3$, LaInO$_3$, BiScO$_3$, and other perovskites of contemporary interest. Differential thermal analysis showed that Ba$_2$ScNbO$_6$ melts at 2165$pm$30{deg}C in an inert atmosphere. Competitive grain growth was visualized by energy dispersive Laue mapping. X-ray diffraction rocking curve measurements revealed full width at half maximum values between 21 and 33 arcsec for 002 and 004 reflections. The crystals were sufficiently large to yield (100)-oriented single-crystal substrates with surface areas as large as 10 x 10 mm$^2$.