The crystallization and magnetic behavior of yttrium iron garnet (YIG) prepared by metallo-organic decomposition (MOD) method are discussed. The chemistry and physics related to synthesis of iron and yttrium carboxylates based on 2-ethylhexanoic acid (2EHA) are studied, since no literature was found which elucidates synthesis of metallo-organic precursor of YIG in spite of the literatures of doped YIG samples such as Bi-YIG. Typically, the metal carboxylates used in preparation of ceramic oxide materials are 2-ethylhexanoate (2EH) solvents. Herein, the synthesis, thermal behavior and solubility of yttrium and iron 2EH used in synthesis of YIG powder by MOD are reported. The crystallization and magnetic parameters, including saturation magnetization and coercivity of these samples, smoothly change as a function of the annealing temperature. It is observed that high sintering temperature of 1300 to 1400 {deg}C promotes the diffraction peaks of YIG, therefore, we can conclude that the formation of YIG in MOD method increases the crystallization temperature. The maximum value of saturation magnetization and minimum value of coercivity and remanence are observed for the sample sintered at 1200{deg}C which are 13.7 emu/g, 10.38 Oe and 1.5 emu/g, respectively. This study cites the drawbacks in chemical synthesis of metallo-organic based YIG production.
قيم البحث
اقرأ أيضاً
We report measurements on yttrium iron garnet (YIG) thin films grown on both gadolinium gallium garnet (GGG) and yttrium aluminium garnet (YAG) substrates, with and without thin Pt top layers. We provide three principal results: the observation of an
interfacial region at the Pt/YIG interface, we place a limit on the induced magnetism of the Pt layer and confirm the existence of an interfacial layer at the GGG/YIG interface. Polarised neutron reflectometry (PNR) was used to give depth dependence of both the structure and magnetism of these structures. We find that a thin film of YIG on GGG is best described by three distinct layers: an interfacial layer near the GGG, around 5 nm thick and non-magnetic, a magnetic bulk phase, and a non-magnetic and compositionally distinct thin layer near the surface. We theorise that the bottom layer, which is independent of the film thickness, is caused by Gd diffusion. The top layer is likely to be extremely important in inverse spin Hall effect measurements, and is most likely Y2O3 or very similar. Magnetic sensitivity in the PNR to any induced moment in the Pt is increased by the existence of the Y2O3 layer; any moment is found to be less than 0.02 uB/atom.
The structural, electronic, and magnetic properties of VSSe, VSeTe, VSTe monolayers in both 2H and 1T phases are investigated via first-principles calculations. The 2H phase is energetically favorable in VSSe and VSeTe, whereas the 1T phase is lower
in energy in VSTe. For V-based Janus monolayers in the 2H phase, calculations of the magnetic anisotropy show an easy-plane for the magnetic moment. As such, they should not exhibit a ferromagnetic phase transition, but instead, a Berezinskii-Kosterlitz-Thouless (BKT) transition. A classical XY model with nearest-neighbor coupling estimates critical temperatures (T$_{BKT}$) ranging from 106 K for VSSe to 46 K for VSTe.
Transparent pure and Cu-doped (2.5, 5 and 10 at. %) anatase TiO2 thin films were grown by pulsed laser deposition technique on LaAlO3 substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The
magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO2. The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to this Cu substitutionally replacing cations in TiO2.
Commercial powder bed fusion additive manufacturing systems use recoaters for the layer-by-layer distribution of powder. Despite the known limitations of recoaters, there has been relatively little work presented on the possible benefits of alternati
ve powder delivery systems. Here, we show the use of a technology using simple vibration to control the powder flow for powder bed additive manufacturing. The capabilities of this approach are illustrated experimentally using two very different powders; a `conventional gas atomized Ti-6Al-4V powder designed for electron beam additive manufacturing and a water atomized Fe-4wt%Ni alloy used in powder metallurgy. Discrete element modelling is used to reveal the mechanisms controlling the dependence of feed rate on feeder process parameters and to investigate the potential strengths and limitations of this approach.
Vanadium tetracyanoethylene (V[TCNE]$_text{x}$) is an organic-based ferrimagnet that exhibits robust magnetic ordering (T$_text{C}$ of over 600 K), high quality-factor (high-Q) microwave resonance (Q up to 3,500), and compatibility with a wide variet
y of substrates and encapsulation technologies. Here, we substantially expand the potential scope and impact of this emerging material by demonstrating the ability to produce engineered nanostructures with tailored magnetic anisotropy that serve as a platform for the exploration of cavity magnonics, revealing strongly coupled quantum confined standing wave modes that can be tuned into and out of resonance with an applied magnetic field. Specifically, time-domain micromagnetic simulations of these nanostructures faithfully reproduce the experimentally measured spectra, including the quasi-uniform mode and higher-order spin-wave (magnon) modes. Finally, when the two dominant magnon modes present in the spectra are brought into resonance by varying the orientation of the in-plane magnetic field, we observe anti-crossing behavior indicating strong coherent coupling between these two magnon modes at room temperature. These results position V[TCNE]$_text{x}$ as a leading candidate for the development of coherent magnonics, with potential applications ranging from microwave electronics to quantum information.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها