We report on the first use of laser ablation to make sub-millimeter, broad-band, anti-reflection coatings (ARC) based on sub-wavelength structures (SWS) on alumina and sapphire. We used a 515 nm laser to produce pyramid-shaped structures with pitch of about 320 $mu$m and total height of near 800 $mu$m. Transmission measurements between 70 and 140 GHz are in agreement with simulations using electromagnetic propagation software. The simulations indicate that SWS ARC with the fabricated shape should have a fractional bandwidth response of $Delta u / u_{center} = 0.55$ centered on 235 GHz for which reflections are below 3%. Extension of the bandwidth to both lower and higher frequencies, between few tens of GHz and few THz, should be straightforward with appropriate adjustment of laser ablation parameters.
قيم البحث
اقرأ أيضاً
We used two novel approaches to produce sub-wavelength structure (SWS) anti-reflection coatings (ARC) on silicon for the millimeter and sub-millimeter (MSM) wave band: picosecond laser ablation and dicing with beveled saws. We produced pyramidal stru
ctures with both techniques. The diced sample, machined on only one side, had pitch and height of 350 $mu$m and 972 $mu$m. The two laser ablated samples had pitch of 180 $mu$m and heights of 720 $mu$m and 580 $mu$m; only one of these samples was ablated on both sides. We present measurements of shape and optical performance as well as comparisons to the optical performance predicted using finite element analysis and rigorous coupled wave analysis. By extending the measured performance of the one-sided diced sample to the two-sided case, we demonstrate 25 % band averaged reflectance of less than 5 % over a bandwidth of 97 % centered on 170 GHz. Using the two-sided laser ablation sample, we demonstrate reflectance less than 5 % over 83 % bandwidth centered on 346 GHz.
Refractive optical elements are widely used in millimeter and sub-millimeter astronomical telescopes. High resistivity silicon is an excellent material for dielectric lenses given its low loss-tangent, high thermal conductivity and high index of refr
action. The high index of refraction of silicon causes a large Fresnel reflectance at the vacuum-silicon interface (up to 30%), which can be reduced with an anti-reflection (AR) coating. In this work we report techniques for efficiently AR coating silicon at sub-millimeter wavelengths using Deep Reactive Ion Etching (DRIE) and bonding the coated silicon to another silicon optic. Silicon wafers of 100 mm diameter (1 mm thick) were coated and bonded using the Silicon Direct Bonding technique at high temperature (1100 C). No glue is used in this process. Optical tests using a Fourier Transform Spectrometer (FTS) show sub-percent reflections for a single-layer DRIE AR coating designed for use at 320 microns on a single wafer. Cryogenic (10 K) measurements of a bonded pair of AR-coated wafers also reached sub-percent reflections. A prototype two-layer DRIE AR coating to reduce reflections and increase bandwidth is presented and plans for extending this approach are discussed.
We designed, fabricated, and measured anti-reflection coating (ARC) on sapphire that has 116% fractional bandwidth and transmission of at least 97% in the millimeter wave band. The ARC was based on patterning pyramid-like sub-wavelength structures (S
WS) using ablation with a 15 W femto-second laser operating at 1030 nm. One side of each of two discs was fabricated with SWS that had a pitch of 0.54 mm and height of 2 mm. The average ablation volume removal rate was 1.6 mm$^{3}$/min. Measurements of the two-disc sandwich show transmission higher than 97% between 43 and 161 GHz. We characterize instrumental polarization (IP) arising from differential transmission due to asymmetric SWS. We find that with proper alignment of the two disc sandwich RMS IP across the band is predicted to be 0.07% at normal incidence, and less than 0.6% at incidence angles up to 20 degrees. These results indicate that laser ablation of SWS on sapphire and on other hard materials such as alumina is an effective way to fabricate broad-band ARC.
The desire for higher sensitivity has driven ground-based cosmic microwave background (CMB) experiments to employ ever larger focal planes, which in turn require larger reimaging optics. Practical limits to the maximum size of these optics motivates
the development of quasi-optically-coupled (lenslet-coupled), multi-chroic detectors. These detectors can be sensitive across a broader bandwidth compared to waveguide-coupled detectors. However, the increase in bandwidth comes at a cost: the lenses (up to $sim$700 mm diameter) and lenslets ($sim$5 mm diameter, hemispherical lenses on the focal plane) used in these systems are made from high-refractive-index materials (such as silicon or amorphous aluminum oxide) that reflect nearly a third of the incident radiation. In order to maximize the faint CMB signal that reaches the detectors, the lenses and lenslets must be coated with an anti-reflective (AR) material. The AR coating must maximize radiation transmission in scientifically interesting bands and be cryogenically stable. Such a coating was developed for the third generation camera, SPT-3G, of the South Pole Telescope (SPT) experiment, but the materials and techniques used in the development are general to AR coatings for mm-wave optics. The three-layer polytetrafluoroethylene-based AR coating is broadband, inexpensive, and can be manufactured with simple tools. The coating is field tested; AR coated focal plane elements were deployed in the 2016-2017 austral summer and AR coated reimaging optics were deployed in 2017-2018.
We report on the development of coatings for a CCD detector optimized for use in a fixed dispersion UV spectrograph. Due to the rapidly changing index of refraction of Si, single layer broadband anti-reflection coatings are not suitable to increase q
uantum efficiency at all wavelengths of interest. Instead, we describe a creative solution that provides excellent performance over UV wavelengths. We describe progress in the development of a CCD detector with theoretical quantum efficiencies (QE) of greater than 60% at wavelengths from 120 to 300nm. This high efficiency may be reached by coating a backside illuminated, thinned, delta-doped CCD with a series of thin film anti-reflection coatings. The materials tested include MgF2 (optimized for highest performance from 120-150nm), SiO2 (150-180nm), Al2O3(180-240nm), MgO (200-250nm), and HfO2 (240-300nm). A variety of deposition techniques were tested and a selection of coatings which minimized reflectance on a Si test wafer were applied to live devices. We also discuss future uses and improvements, including graded and multi-layer coatings.