تسجيل مستخدم جديدAppearance of bulk Superconductivity under Hydrostatic Pressure in Sr0.5RE0.5FBiS2 (RE = Ce, Nd, Pr and Sm) compounds
120
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report the appearance of superconductivity under hydrostatic pressure (0.35 to 2.5GPa) in Sr0.5RE0.5FBiS2 with RE = Ce, Nd, Pr and Sm. The studied compounds, synthesized by solid state reaction route, are crystallized in tetragonal P4/nmm space group. At ambient pressure though the RE = Ce exhibit the onset of superconductivity below 2.5K, the Nd, Pr and Sm samples are not superconducting down to 2K. With application of hydrostatic pressure (up to 2.5GPa), superconducting transition temperature is increased to around 10K for all the studied samples. The magneto-transport measurements are carried out on all the samples with maximum Tc i.e., at under 2.5GPa pressure and their upper critical fields are determined. The new superconducting compounds appear to be quite robust against magnetic field but within Pauli paramagnetic limit. The new superconducting compounds with various RE (Ce, Nd, Pr and Sm) belonging to Sr0.5La0.5FBiS2 family are successfully synthesized for the first time and superconductivity is induced in them under hydrostatic pressure.
قيم البحث
اقرأ أيضاً
Polycrystalline samples of Sr1-xRExFBiS2 (RE: La, Ce, Pr, Nd, and Sm) were synthesized via the solid-state reaction and characterized using synchrotron X-ray diffraction. Although all the Sr0.5RE0.5FBiS2 samples exhibited superconductivity at transit
ion temperatures (Tc) within the range of 2.1-2.7 K under ambient pressure, the estimated superconducting volume fraction was small. This indicated the non-bulk nature of superconductivity in these samples under ambient pressure. A dramatic evolution of the bulk superconducting phases was achieved on applying an external hydrostatic pressure. Near pressures below 1 GPa, bulk superconductivity was induced with a Tc of 2.5-2.8 K, which is termed as the low-P phase. Moreover, the high-P phase (Tc = 10.0-10.8 K) featuring bulk characteristics was observed at higher pressures. Pressure-Tc phase diagrams indicated that the critical pressure for the emergence of the high-P phase tends to increase with decreasing ionic radius of the doped RE ions. According to the high-pressure X-ray diffraction measurements of Sr0.5La0.5FBiS2, a structural phase transition from tetragonal to monoclinic also occurred at approximately 1.1 GPa. Thus, this phase transition indicates a pressure-induced superconducting-superconducting transition similar to the transition in LaO0.5F0.5BiS2. Bulk superconducting phases in Sr0.5RE0.5FBiS2 induced by the external hydrostatic pressure effect are expected to be useful for evaluating the mechanisms of superconductivity in BiCh2-based superconductors.
Here we report pressure effect on superconducting transition temperature (Tc) of ReFeAsO0.85 (Re= Sm and Nd) system without fluorine doping. In-situ measurements under high pressure showed that Tc of the two compounds decrease monotonously over the p
ressure range investigated. The pressure coefficients dTc/dP in SmFeAsO0.85 and Nd FeAsO0.85 were different, revealing the important influence of the deformation in layers on Tc. Theoretical calculations suggested that the electron density of states decrease with increasing pressure, following the same trend of experimental data.
We study the impact of hydrostatic pressure on superconductivity of new BiS2 based layered REO0.5F0.5BiS2 (RE-La, Pr, and Nd) compounds through the measurements of dc electrical resistivity. The REO0.5F0.5BiS2 (RE-La, Pr and Nd) compounds synthesized
by solid state reaction route via vacuum encapsulation are crystallized in the tetragonal P4/nmm space group. At ambient pressure the superconducting transition onset temperatures are 2.7K, 3.5K and 4.5K which are enhanced substantially under external hydrostatic pressure to 10.5K, 7.8K and 7.5K for LaO0.5F0.5BiS2, PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2 respectively at 1.68GPa. The normal state electrical resistivity decreases with applied pressure for REO0.5F0.5BiS2 (RE-La, Pr and Nd). The electrical resistivity under magnetic field and applied pressure has been measured to estimate upper critical field, the values of which are 15.9Tesla, 8.8Tesla and 8.2Tesla for LaO0.5F0.5BiS2, PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2 compounds. Substantial enhancement of superconductivity under moderate pressures in studied new BiS2 based superconductors call for the attention of condensed matter physics community.
A new crystal growth technique for single-crystals of REFeAsO (RE = La, Ce, Pr, Nd, Sm, Gd, and Tb) using NaI/KI as flux is presented. Crystals with a size up to 300 $mu$m were isolated for single-crystal X-ray diffraction measurements. Lattice param
eters were determined by LeBail fits of X-ray powder data against LaB6 standard. A consistent set of structural data is obtained and interpreted in a hard-sphere model. Effective radii for the rare-earth metal atoms for REFeAsO are deduced. The relation of the intra- and inter-plane distances of the arsenic atoms is identified as limiter of the phase formation, and its influence on Tc is discussed.
Measurements of electrical resistivity were performed between 3 and 300 K at various pressures up to 2.8 GPa on the BiS2-based superconductors LnO0.5F0.5BiS2 (Ln = Pr, Nd). At lower pressures, PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2 exhibit superconductivi
ty with critical temperatures Tc of 3.5 and3.9 K, respectively. As pressure is increased, both compounds undergo a transition at a pressure Pt from a low Tc superconducting phase to a high Tc superconducting phase in which Tc reaches maximum values of 7.6 and 6.4 K for PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2, respectively. The pressure-induced transition is characterized by a rapid increase in Tc within a small range in pressure of ~0.3 GPa for both compounds. In the normal state of PrO0.5F0.5BiS2, the transition pressure Pt correlates with the pressure where the suppression of semiconducting behaviour saturates. In the normal state of NdO0.5F0.5BiS2, Pt is coincident with a semiconductor-metal transition. This behaviour is similar to the results recently reported for the LnO0.5F0.5BiS2 (Ln = La, Ce) compounds. We observe that Pt and the size of the jump in Tc between the two superconducting phases both scale with the lanthanide element in LnO0.5F0.5BiS2 (Ln = La, Ce, Pr, Nd).