تسجيل مستخدم جديدGraphene Nanoribbon Field-Effect Transistors on Wafer-Scale Epitaxial Graphene on SiC substrates
137
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report the realization of top-gated graphene nanoribbon field effect transistors (GNRFETs) of ~10 nm width on large-area epitaxial graphene exhibiting the opening of a band gap of ~0.14 eV. Contrary to prior observations of disordered transport and severe edge-roughness effects of GNRs, the experimental results presented here clearly show that the transport mechanism in carefully fabricated GNRFETs is conventional band-transport at room temperature, and inter-band tunneling at low temperature. The entire space of temperature, size, and geometry dependent transport properties and electrostatics of the GNRFETs are explained by a conventional thermionic emission and tunneling current model. Our combined experimental and modeling work proves that carefully fabricated narrow GNRs behave as conventional semiconductors, and remain potential candidates for electronic switching devices.
قيم البحث
اقرأ أيضاً
This paper describes the behavior of top gated transistors fabricated using carbon, particularly epitaxial graphene on SiC, as the active material. In the past decade research has identified carbon-based electronics as a possible alternative to silic
on-based electronics. This enthusiasm was spurred by high carbon nanotube carrier mobilities. However, nanotube production, placement, and control are all serious issues. Graphene, a thin sheet of graphitic carbon, can overcome some of these problems and therefore is a promising new electronic material. Although graphene devices have been built before, in this work we provide the first demonstration and systematic evaluation of arrays of a large number of transistors entirely produced using standard microelectronics methods. Graphene devices presented feature high-k dielectric, mobilities up to 5000 cm2/Vs and, Ion/Ioff ratios of up to 7, and are methodically analyzed to provide insight into the substrate properties. Typical of graphene, these micron-scale devices have negligible band gaps and therefore large leakage currents.
We present an atomistic three-dimensional simulation of graphene nanoribbon field effect transistors (GNR-FETs), based on the self-consistent solution of the 3D Poisson and Schroedinger equation with open boundary conditions within the non-equilibriu
m Greens Function formalism and a tight-binding hamiltonian. With respect to carbon nanotube FETs, GNR-FETs exhibit comparable performance, reduced sensitivity on the variability of channel chirality, and similar leakage problems due to band-to-band tunneling. Acceptable transistor performance requires effective nanoribbon width of 1-2 nm, that could be obtained with periodic etching patterns or stress patterns.
High-performance graphene field-effect transistors have been fabricated on epitaxial graphene synthesized on a two-inch SiC wafer, achieving a cutoff frequency of 100 GHz for a gate length of 240 nm. The high-frequency performance of these epitaxial
graphene transistors not only shows the highest speed for any graphene devices up to date, but it also exceeds that of Si MOSFETs at the same gate length. The result confirms the high potential of graphene for advanced electronics applications, marking an important milestone for carbon electronics.
We have developed metal-oxide graphene field-effect transistors (MOGFETs) on sapphire substrates working at microwave frequencies. For monolayers, we obtain a transit frequency up to ~ 80 GHz for a gate length of 200 nm, and a power gain maximum freq
uency of about ~ 3 GHz for this specific sample. Given the strongly reduced charge noise for nanostructures on sapphire, the high stability and high performance of this material at low temperature, our MOGFETs on sapphire are well suited for a cryogenic broadband low-noise amplifier.
Up to two layers of epitaxial graphene have been grown on the Si-face of two-inch SiC wafers exhibiting room-temperature Hall mobilities up to 1800 cm^2/Vs, measured from ungated, large, 160 micron x 200 micron Hall bars, and up to 4000 cm^2/Vs, from
top-gated, small, 1 micron x 1.5 micron Hall bars. The growth process involved a combination of a cleaning step of the SiC in a Si-containing gas, followed by an annealing step in Argon for epitaxial graphene formation. The structure and morphology of this graphene has been characterized using AFM, HRTEM, and Raman spectroscopy. Furthermore, top-gated radio frequency field effect transistors (RF-FETs) with a peak cutoff frequency fT of 100 GHz for a gate length of 240 nm were fabricated using epitaxial graphene grown on the Si face of SiC that exhibited Hall mobilities up to 1450 cm^2/Vs from ungated Hall bars and 1575 cm^2/Vs from top-gated ones. This is by far the highest cut-off frequency measured from any kind of graphene.