We present transport measurement results on superconducting Nb films with diluted triangular arrays (honeycomb and kagom{e}) of holes. The patterned films have large disk-shaped interstitial regions even when the edge-to-edge separations between nearest neighboring holes are comparable to the coherence length. Changes in the field interval of two consecutive minima in the field dependent resistance $R(H)$ curves are observed. In the low field region, fine structures in the $R(H)$ and $T_c(H)$ curves are identified in both arrays. Comparison of experimental data with calculation results shows that these structures observed in honeycomb and kagom{e} hole arrays resemble those in wire networks with triangular and $T_3$ symmetries, respectively. Our findings suggest that even in these specified periodic hole arrays with very large interstitial regions, the low field fine structures are determined by the connectivity of the arrays
قيم البحث
اقرأ أيضاً
We study experimentally the critical depinning current Ic versus applied magnetic field B in Nb thin films which contain 2D arrays of circular antidots placed on the nodes of quasiperiodic (QP) fivefold Penrose lattices. Close to the transition tempe
rature Tc we observe matching of the vortex lattice with the QP pinning array, confirming essential features in the Ic(B) patterns as predicted by Misko et al. [Phys. Rev. Lett, vol.95, 177007 (2005)]. We find a significant enhancement in Ic(B) for QP pinning arrays in comparison to Ic in samples with randomly distributed antidots or no antidots.
The depinning current Ic versus applied magnetic field B close to the transition temperature Tc of Nb thin films with randomly diluted triangular arrays of antidots is investigated. % Our experiments confirm essential features in Ic(B) as predicted b
y Reichhardt and Olson Reichhardt [Phys.Rev. B 76, 094512 (2007)]. % We show that, by introducing disorder into periodic pinning arrays, Ic can be enhanced. % In particular, for arrays with fixed density n_p of antidots, an increase in dilution Pd induces an increase in Ic and decrease of the flux-flow voltage for B>Bp=n_p Phi_0.
Nb films containing extended arrays of holes with 45-nm diameter and 100-nm spacing have been fabricated using anodized aluminum oxide (AAO) as substrate. Pronounced matching effects in the magnetization and Little-Parks oscillations of the supercond
ucting critical temperature have been observed in fields up to 9 kOe. Flux pinning in the patterned samples is enhanced by two orders of magnitude as compared to unpatterned reference samples in applied fields exceeding 5 kOe. Matching effects are a dominant contribution to vortex pinning at temperatures as low as 4.2 K due to the extremely small spacing of the holes.
We report on a study of the structural, magnetic and superconducting properties of Nb(25nm)/Gd($d_f$)/Nb(25nm) hybrid structures of a superconductor/ ferromagnet (S/F) type. The structural characterization of the samples, including careful determinat
ion of the layer thickness, was performed using neutron and X-ray scattering with the aid of depth sensitive mass-spectrometry. The magnetization of the samples was determined by SQUID magnetometry and polarized neutron reflectometry and the presence of magnetic ordering for all samples down to the thinnest Gd(0.8nm) layer was shown. The analysis of the neutron spin asymmetry allowed us to prove the absence of magnetically dead layers in junctions with Gd interlayer thickness larger than one monolayer. The measured dependence of the superconducting transition temperature $T_c(d_f)$ has a damped oscillatory behavior with well defined positions of the minimum at $d_f$=3nm and the following maximum at $d_f$=4nm; the behavior, which is in qualitative agreement with the prior work (J.S. Jiang et al, PRB 54, 6119). The analysis of the $T_c(d_f)$ dependence based on Usadel equations showed that the observed minimum at $d_f$=3nm can be described by the so called $0$ to $pi$ phase transition of highly transparent S/F interfaces with the superconducting correlation length $xi_f approx 4$nm in Gd. This penetration length is several times higher than for strong ferromagnets like Fe, Co or Ni, simplifying thus preparation of S/F structures with $d_f sim xi_f$ which are of topical interest in superconducting spintronics.
Flux penetrations into three-dimensional Nb superconducting strip arrays, where two layers of strip arrays are stacked by shifting a half period, are studied using a magneto-optical imaging method. Flux avalanches are observed when the overlap betwee
n the top and bottom layers is large even if the width of each strip is well below the threshold value. In addition, anomalous linear avalanches perpendicular to the strip are observed in the shifted strip array when the overlap is very large and the thickness of the superconductor is greater than the penetration depth. We discuss possible origins for the flux avalanches, including linear ones, by considering flux penetration calculated by the Campbell method assuming the Bean model.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها