Spin-flip mechanism in Ag nanowires with MgO surface protection layers has been investigated by means of nonlocal spin valve measurements using Permalloy/Ag lateral spin valves. The spin flip events mediated by surface scattering are effectively suppressed by the MgO capping layer. The spin relaxation process was found to be well described in the framework of Elliott-Yafet mechanism and then the probabilities of spin-filp scattering for phonon or impurity mediated momentum scattering is precisely determined in the nanowires. The temperature dependent spin-lattice relaxation follows the Bloch-Gruneisen theory and falls on to a universal curve for the monovalent metals as in the Monod and Beuneu scaling determined from the conduction electron spin resonance data for bulk.
قيم البحث
اقرأ أيضاً
Spin-orbit interaction (SOI) plays a key role in creating Majorana zero modes in semiconductor nanowires proximity coupled to a superconductor. We track the evolution of the induced superconducting gap in InSb nanowires coupled to a NbTiN superconduc
tor in a large range of magnetic field strengths and orientations. Based on realistic simulations of our devices, we reveal SOI with a strength of 0.15-0.35 eV$require{mediawiki-texvc}AA$. Our approach identifies the direction of the spin-orbit field, which is strongly affected by the superconductor geometry and electrostatic gates.
The possibility of transporting spin information over long distances in graphene, owing to its small intrinsic spin-orbit coupling (SOC) and the absence of hyperfine interaction, has led to intense research into spintronic applications. However, meas
ured spin relaxation times are orders of magnitude smaller than initially predicted, while the main physical process for spin dephasing and its charge-density and disorder dependences remain unconvincingly described by conventional mechanisms. Here, we unravel a spin relaxation mechanism for nonmagnetic samples that follows from an entanglement between spin and pseudospin driven by random SOC, which makes it unique to graphene. The mixing between spin and pseudospin-related Berrys phases results in fast spin dephasing even when approaching the ballistic limit, with increasing relaxation times away from the Dirac point, as observed experimentally. The SOC can be caused by adatoms, ripples or even the substrate, suggesting novel spin manipulation strategies based on the pseudospin degree of freedom.
We have studied spin relaxation characteristics in a Ag nanowire covered with various oxide layers of Bi2O3, Al2O3, HfO2, MgO or AgOx by using non-local spin valve structures. The spin-flip probability, a ratio of momentum relaxation time to spin rel
axation time at 10 K, exhibits a gradual increase with an atomic number of the oxide constituent elements, Mg, Al, Ag and Hf. Surprisingly the Bi2O3 capping was found to increase the probability by an order of magnitude compared with other oxide layers. This finding suggests the presence of an additional spin relaxation mechanism such as Rashba effect at the Ag/Bi2O3 interface, which cannot be explained by the simple Elliott-Yafet mechanism via phonon, impurity and surface scatterings. The Ag/Bi2O3 interface may provide functionality as a spin to charge interconversion layer.
The contributions to the spin relaxation in copper (Cu) nanowires are quantified by carefully analyzing measurements of both charge and spin transport in lateral spin valves as a function of temperature and thickness. The temperature dependence of th
e spin-flip scattering solely arises from the scattering with phonons, as in bulk Cu, whereas we identify grain boundaries as the main temperature-independent contribution of the defects in the nanowires. A puzzling maximum in the spin diffusion length of Cu at low temperatures is found, which can be explained by the presence of magnetic impurities. The results presented here suggest routes for improving spin transport in metallic nanostructures, otherwise limited by confinement effects.
Narrow-bandgap III-V semiconductor nanowires (NWs) with a suitable band structure and strong light-trapping ability are ideal for high-efficiency low-cost solar water-splitting systems. However, due to their nanoscale dimension, they suffer more seve
re corrosion by the electrolyte solution than the thin-film counterparts. Thus, short-term durability is the major obstacle for using these NWs for practical water splitting applications. Here, we demonstrated for the first time that a thin layer (~7 nm thick) of compact TiO$_2$ deposited by atomic layer deposition can provide robust protection to III-V NWs. The protected GaAs NWs maintain 91.4% of its photoluminescence intensity after 14 months of storage in ambient atmosphere, which suggests the TiO$_2$ layer is pinhole-free. Working as a photocathode for water splitting, they exhibited a 45% larger photocurrent density compared with un-protected counterparts and a high Faraday efficiency of 91%, and can also maintain a record-long highly-stable performance among narrow-bandgap III-V NW photoelectrodes; after 67 hours photoelectrochemical stability test reaction in strong acid electrolyte solution (pH = 1), they show no apparent indication of corrosion, which is in stark contrast to the un-protected NWs that are fully failed after 35-hours. These findings provide an effective way to enhance both stability and performance of III-V NW based photoelectrodes, which are highly important for practical applications in solar-energy-based water splitting systems.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها