Pulsed laser deposition of SrTiO3/LaGaO3 and SrTiO3/LaAlO3 interfaces has been analyzed with a focus on the kinetic energy of the ablated species. LaGaO3 and LaAlO3 plasma plumes were studied by fast photography and space-resolved optical emission spectroscopy. Reflection high energy electron diffraction was performed proving a layer-by-layer growth up to 10-1 mbar oxygen pressure. The role of the energetic plasma plume on the two-dimensional growth and the presence of interfacial defects at different oxygen growth pressure has been discussed in view of the conducting properties developing at such polar/non-polar interfaces.
قيم البحث
اقرأ أيضاً
The crystal structures of LaAlO3 films grown by pulsed laser deposition on SrTiO3 substrates at oxygen pressure of 10-3 mbar or 10-5 mbar, where kinetics of ablated species hardly depend on oxygen background pressure, are compared. Our results show t
hat the interface between LaAlO3 and SrTiO3 is sharper when the oxygen pressure is lower. Over time, the formation of various crystalline phases is observed while the crystalline thickness of the LaAlO3 layer remains unchanged. X-ray scattering as well as atomic force microscopy measurements indicate three-dimensional growth of such phases, which appear to be fed from an amorphous capping layer present in as-grown samples.
The hysteretic piezoelectric response in LaAlO3/SrTiO3 heterostructures can provide important insights into the mechanism for interfacial conductance and its metastability under various conditions. We have performed a variety of nonlocal piezoelectri
c force microscopy experiments on 3 unit cell LaAlO3/SrTiO3 heterostructures. A hysteretic piezoresponse is observed under various environmental and driving conditions. The hysteresis is suppressed when either the sample is placed in vacuum or the interface is electrically grounded. We present a simple physical model which can account for the observed phenomena.
We show that the growth of the heterostructure LaGaO3/SrTiO3 yields the formation of a highly conductive interface. Our samples were carefully analyzed by high resolution electron microscopy, in order to assess their crystal perfection and to evaluat
e the abruptness of the interface. Their carrier density and sheet resistance are compared to the case of LaAlO3/SrTiO3 and a superconducting transition is found. The results open the route to widening the field of polar-non polar interfaces, pose some phenomenological constrains to their underlying physics and highlight the chance of tailoring their properties for future applications by adopting suitable polar materials.
The surface structure of SrTiO3(001) thin films homoepitaxially grown by PLD in step-flow mode was characterized using low temperature STM. It was found that one-dimensional (1D) TiOx-based nanostructures were formed on the thin film surface and thei
r density increased with increasing thin film thickness. Most of the 1D nanostructures disappeared after a post-deposition annealing, indicating that this structure is metastable due to the nonequilibrium growth mode. The resulting surface after annealing exhibited similar features to that of a thinner film, having a domain structure with (2x1) and (1x2) reconstructions, but with fewer oxygen-vacancy-type defects. These results imply that the step-flow growth is likely to produce TiOx-rich surface and Ti deficiencies in the film. By the post-deposition annealing, the rich TiOx would diffuse from the surface into the film to compensate defects associated with Ti vacancies and oxygen vacancies, resulting in the stable surface structure with fewer oxygen vacancies. Thus, STM measurements can provide us with a microscopic picture of surface stoichiometry of thin films originating in the dynamics of the growth process, and can present a new approach for designing functional oxide films.
Cu2Ta4O12 (CTaO) thin films were successfully deposited on Si(100) substrates by pulsed-laser deposition technique. The crystalline structure and the surface morphology of the CTaO thin films were strongly affected by substrate temperature, oxygen pr
essure and target - substrate distance. In general during deposition of CTaO the formation of a Ta2O5 phase appeared, on which CTaO grew with different orientations. We report on the experimental set-up, details for film deposition and the film properties determined by SEM, EDX and XRD.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها