We synthesized Sr-doped $La_{0.85}Sr_{0.15}OFeAs$ sample with single phase, and systematically studied the effect of oxygen deficiency in the Sr-doped LaOFeAs system. It is found that substitution of Sr for La indeed induces the hole carrier evidenced by positive thermoelectric power (TEP), but no bulk superconductivity is observed. The superconductivity can be realized by annealing the as-grown sample in vacuum to produce the oxygen deficiency. With increasing the oxygen deficiency, the superconducting transition temperature ($T_c$) increases and maximum $T_c$ reaches about 26 K the same as that in La(O,F)FeAs. TEP dramatically changes from positive to negative in the nonsuperconducting as-grown sample to the superconducting samples with oxygen deficiency. While $R_H$ is always negative for all samples (even for Sr-doped as grown sample). It suggests that the $La_{0.85}Sr_{0.15}O_{1-delta}FeAs$ is still electron-type superconductor.
قيم البحث
اقرأ أيضاً
We report the Se substitution effects on the crystal structure, superconducting properties, and valence states of self-doped BiCh2-based compound CeOBiS2-xSex. Polycrystalline CeOBiS2-xSex samples with x = 0-1.0 were synthesized. For x = 0.4 and 0.6,
bulk superconducting transitions with a large shielding volume fraction were observed in magnetic susceptibility measurements; the highest transition temperature (Tc) was 3.0 K for x = 0.6. A superconductivity phase diagram of CeOBiS2-xSex was established based on Tc estimated from the electrical resistivity and magnetization measurements. The emergence of superconductivity in CeOBiS2-xSex was explained with two essential parameters of in-plane chemical pressure and carrier concentration, which systematically changed with increasing Se concentration.
Strontium intercalation between van der Waals bonded layers of topological insulator Bi2Se3 is found to induce superconductivity with a maximum Tc of 2.9 K. Transport measurement on single crystal of optimally doped sample Sr0.1Bi2Se3 shows weak anis
otropy (1.5) and upper critical field Hc2(0) equals to 2.1 T for magnetic field applied per-pendicular to c -axis of the sample. The Ginzburg-Landau coherence lengths are Xi-ab = 15.3 {AA} and Xi_c = 10.2 {AA}. The lower critical field and zero temperature penetration depth Lambda(0) are estimated to be 0.35 mT and 1550 nm respectively. Hall and Seebeck measurements confirm the dominance of electronic conduction and the carrier concentration is surprisingly low (n = 1.85 x 10^19 cm-3) at 10 K indicating possibility of unconventional superconductivity.
We have performed a systematic angle-resolved photoemission study of as-grown and oxygen-reduced Pr$_{2-x}$Ce$_x$CuO$_4$ and Pr$_{1-x}$LaCe$_{x}$CuO$_4$ electron-doped cuprates. In contrast to the common belief, neither the band filling nor the band
parameters are significantly affected by the oxygen reduction process. Instead, we show that the main electronic role of the reduction process is to remove an anisotropic leading edge gap around the Fermi surface. While the nodal leading edge gap is induced by long-range antiferomagnetic order, the origin of the antinodal one remains unclear.
Electron-doped and hole-doped superconducting cuprates exhibit a symmetric phase diagram as a function of doping. This symmetry is however only approximate. Indeed, electron-doped cuprates become superconductors only after a specific annealing proces
s: This annealing affects the oxygen content only by a tiny amount, but has a dramatic impact on the electronic properties of the sample. Here, we report the occurrence of superconductivity in oxygen-deficient Nd$_{2-x}$Ce$_x$CuO$_4$ thin films grown in oxygen-free environment, after annealing in pure argon flow. As verified by x-ray diffraction, annealing induces an increase of the interlayer distance between CuO$_2$ planes in the crystal structure. Since this distance is correlated to the concentration of oxygens in apical positions, and since oxygen content cannot substantially increase during annealing, our experiments indicate that the superconducting phase transition has to be ascribed to a migration of oxygen ions to apical positions during annealing. Moreover, as we confirm via first-principles density functional theory calculations, the changes in the structural and transport properties of the films can be theoretically described by a specific redistribution of the existing oxygens ions at apical positions with respect to CuO$_2$ planes, which remodulates the electronic band structure and suppresses the antiferromagnetic order, allowing the emergence of hole superconductivity.
The search for non-centrosymmetric superconductors that may exhibit unusual physical properties and unconventional superconductivity has yielded the synthesis of a non-centrosymmetric phosphide Mg$_2$Rh$_3$P with an Al$_2$Mo$_3$C-type structure. Alth
ough stoichiometric Mg$_2$Rh$_3$P does not exhibit superconductivity at temperatures above 2 K, we found that an Mg deficiency of approximately 5 at.% in the Mg$_2$Rh$_3$P induced superconductivity at 3.9 K. Physical properties such as the lattice parameter a = 0.70881 nm, Sommerfeld constant $gamma_n$ = 5.36 mJ mol$^{-1}$ K$^{-2}$, specific heat jump $Delta$C$_{el}$/$gamma_n$Tc = 0.72, electron-phonon coupling constant $lambda$$_{e-p}$ = 0.58, upper critical field H$_{c2}$(0) = 24.3 kOe, and pressure effect dTc/dP = -0.34 K/GPa were measured for the superconducting Mg$_{2-delta}$Rh$_3$P ($delta$ $sim$ 0.1). Band-structure calculations indicate that exotic fermions, which are not present in high-energy physics, exist in Mg$_2$Rh$_3$P. Since Mg, Rh, and P are the first elements used at each crystal site of Al$_2$Mo$_3$C-type compounds, the discovery of Mg$_2$Rh$_3$P may guide the search for new related materials.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها