تسجيل مستخدم جديدStructure, magnetic and transport properties of Ti-substituted La0.7Sr0.3MnO3
103
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Ti-substituted perovskites, La0.7Sr0.3Mn1-xTixO3, with x between 0 to 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a, c and the unit cell volume increase with increasing Ti content. However, at 10 K, the cell parameter a has a maximum value for x = 0.10, and decreases for x greater than 0.10, while the unit cell volume remains nearly constant for x greater than 0.10. The average (Mn,Ti)-O bond length increases up to x=0.15, and the (Mn,Ti)-O-(Mn,Ti) bond angle decreases with increasing Ti content to its minimum value at x=0.15 at room temperature. Below the Curie temperature T_C, the resistance exhibits metallic behavior for the x _ 0.05 samples. A metal (semiconductor) to insulator transition is observed for the x_ 0.10 samples. A peak in resistivity appears below T_C for all samples, and shifts to a lower temperature as x increases. The substitution of Mn by Ti decreases the 2p-3d hybridization between O and Mn ions, reduces the bandwidth W, and increases the electron-phonon coupling. Therefore, the TC shifts to a lower temperature and the resistivity increases with increasing Ti content. A field-induced shift of the resistivity maximum occurs at x less than or equal to 0.10. The maximum MR effect is about 70% for La0.7Sr0.3Mn0.8Ti0.2O3. The separation of TC and the resistivity maximum temperature Tmax enhances the MR effect in these compounds due to the weak coupling between the magnetic ordering and the resistivity as compared with La0.7Sr0.3MnO3.
قيم البحث
اقرأ أيضاً
The effects of Cu-doping on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1-xCuxO3 (0 < x < 0.20) have been studied using neutron diffraction, magnetization and magnetoresistance (MR) measurements. All samples show the rhombohedra
l structure with the R3c space-group from 10K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state in these compounds. The substitution of Mn by Cu affects the Mn-O bond length and Mn-O-Mn bond angle resulting from the minimization of the distortion of the MnO6 octahedron. Resistivity measurements show that a metal to insulator transition occurs for the x more than 0.15 samples. The x = 0.15 sample shows the highest MR(_80%), which might result from the co-existence of Cu3+/Cu2+ and the dilution effect of Cu-doping on the double exchange interaction.
We discuss the effects of local structure on the electrical transport and magnetic properties of La(0.67)Ca(0.33)Mn(1-x)Ti(x)O(3) system.Based on the intercomparison of the structure, transport and magnetic properties of the Mn site substituted La(0.
67)Ca(0.33)MnO(3) with isovalent diamagnetic and paramagnetic ions, we argue that local structural effects have a decisive role to play, compared to the local spin coupling effects, in the ferromagnetic-metallic ground state of the CMR manganites
Nanostructured permanent magnets are gaining increasing interest and importance for applications such as generators and motors. Thermal management is a key concern since performance of permanent magnets decreases with temperature. We investigated the
magnetic and thermal transport properties of rare-earth free nanostructured SrFe12O19 magnets produced by the current activated pressure assisted densification. The synthesized magnets have aligned grains such that their magnetic easy axis is perpendicular to their largest surface area to maximize their magnetic performance. The SrFe12O19 magnets have fine grain sizes in the cross-plane direction and substantially larger grain sizes in the in-plane direction. It was found that this microstructure results in approximately a factor of two higher thermal conductivity in the in-plane direction, providing an opportunity for effective cooling. The phonons are the dominant heat carriers in this type of permanent magnets near room temperature. Temperature and direction dependent thermal conductivity measurements indicate that both Umklapp and grain boundary scattering are important in the in-plane direction, where the characteristic grain size is relatively large, while grain boundary scattering dominates the cross-plane thermal transport. The investigated nano/microstructural design strategy should translate well to other material systems and thus have important implications for thermal management of nanostructured permanent magnets.
Hexagonal rare-earth ferrite RFeO$_3$ family represents a unique class of multiferroics exhibiting weak ferromagnetism, and a strong coupling between magnetism and structural trimerization is predicted. However, the hexagonal structure for RFeO$_3$ r
emains metastable in conventional condition. We have succeeded in stabilizing the hexagonal structure of polycrystalline YbFeO$_3$ by partial Sc substitution of Yb. Using bulk magnetometry and neutron diffraction, we find that Yb$_{0.42}$Sc$_{0.58}$FeO$_3$ orders into a canted antiferromagnetic state with the Neel temperature $T_N$ ~ 165 K, below which the $Fe^{3+}$ moments form the triangular configuration in the $ab$-plane and their in-plane projections are parallel to the [100] axis, consistent with magnetic space group $P$6$_{3}$$cm$. It is determined that the spin-canting is aligned along the $c$-axis, giving rise to the weak ferromagnetism. Furthermore, the $Fe^{3+}$ moments reorient toward a new direction below reorientation temperature $T_R$ ~ 40 K, satisfying magnetic subgroup $P$6$_{3}$, while the $Yb^{3+}$ moments order independently and ferrimagnetically along the $c$-axis at the characteristic temperature $T_{Yb}$ ~ 15 K. Interestingly, reproducible modulation of electric polarization induced by magnetic field at low temperature is achieved, suggesting that the delicate structural distortion associated with two-up/one-down buckling of the Yb/Sc-planes and tilting of the FeO$_5$ bipyramids may mediate the coupling between ferroelectric and magnetic orders under magnetic field. The present work represents a substantial progress to search for high-temperature multiferroics in hexagonal ferrites and related materials.
The composition dependence of the structural, magnetic, and transport properties of epitaxially grown Mn-Co-Ga films were investigated. The crystal structure was observed to change from tetragonal to cubic as the Co content was increased. In terms of
the dependence of saturation magnetization on the Co content, relatively small value was obtained for the Mn$_{2.3}$Co$_{0.4}$Ga$_{1.3}$ film at a large {it K}$_textrm u$ value of 9.2 Merg/cm$^3$. Electrical resistivity of Mn-Co-Ga films was larger than that of pure Mn-Ga film. The maximum value of the resistivity was 490 $muOmega$cm for Mn$_{2.2}$Co$_{0.6}$Ga$_{1.2}$ film. The high resistivity of Mn-Co-Ga might be due to the presence of localized electron states in the films due to chemical disordering caused by the Co substitution.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها