Ni-Mn-Ga is interesting as a prototype of a magnetic shape-memory alloy showing large magnetic field induced strains. We present here results for the magnetic ordering of Mn-rich Ni-Mn-Ga alloys based on both experiments and theory. Experimental trends for the composition dependence of the magnetization are measured by a vibrating sample magnetometer (VSM) in magnetic fields of up to several tesla and at low temperatures. The saturation magnetization has a maximum near the stoichiometric composition and it decreases with increasing Mn content. This unexpected behaviour is interpreted via first-principles calculations within the density-functional theory. We show that extra Mn atoms are antiferromagnetically aligned to the other moments, which explains the dependence of the magnetization on composition. In addition, the effect of Mn doping on the stabilization of the structural phases and on the magnetic anisotropy energy is demonstrated.
The different crystal structures of ferromagnetic Ni$_2$MnGa have been calculated using density functional theory (DFT) with special emphasis on the modulated structures 10M and 14M. These are important for understanding the stability of Ni$_2$MnGa m
Ultraviolet-photoemission (UPS) measurements and supporting specific-heat, thermal-expansion, resistivity and magnetic-moment measurements are reported for the magnetic shape-memory alloy Ni$_2$MnGa over the temperature range $100K < T < 250K$. All m
Magnetic shape memory Heusler alloys are multiferroics stabilized by the correlations between electronic, magnetic and structural order. To study these correlations we use time resolved x-ray diffraction and magneto-optical Kerr effect experiments to
The stability of the nonmodulated martensitic phase, the austenitic Fermi surface and the phonon dispersion relations for ferromagnetic Ni$_2$MnGa are studied using density functional theory. Exchange-correlation effects are considered with various d
Mn$_2$Au is an important antiferromagnetic (AF) material for spintronics applications. Due to its very high Neel temperature of about 1500 K, some of the basic properties are difficult to explore, such as the AF susceptibility and the exchange consta