We report dc transport and magnetization measurements of Jc in MgB2 wires fabricated by the powder-in-tube method, using commercial MgB2 powder with 5 %at Mg powder added as an additional source of magnesium, and stainless steel as sheath material. By appropriate heat treatments, we have been able to increase Jc by more than one order of magnitude from that of the as-drawn wire. We show that one beneficial effect of the annealing is the elimination of most of the micro-cracks, and we correlate the increase in Jc with the disappearance of the weak-link-type behavior.
قيم البحث
اقرأ أيضاً
The critical current density (Jc) of hot isostatic pressed (HIPed) MgB2 wires, measured by d.c. transport and magnetization, is compared with that of similar wires annealed at ambient pressure. The HIPed wires have a higher Jc than the annealed wires
, especially at high temperatures and magnetic fields, and higher irreversibility field (Hirr). The HIPed wires are promising for applications, with Jc>106 A/cm2 at 5 K and zero field and >104 A/cm2 at 1.5 T and 26.5 K, and Hirr ~ 17 T at 4 K. The improvement is attributed to a high density of structural defects, which are the likely source of vortex pinning. These defects, observed by transmission electron microscopy, include small angle twisting, tilting, and bending boundaries, resulting in the formation of sub-grains within MgB2 crystallites.
The influence of the nature of the boron precursor on the superconducting properties of polycrystalline MgB2 was studied. Critical current densities for the MgB2 made from high purity amorphous boron are at least a factor of three higher than typical
values measured for standard MgB2 samples made from amorphous precursors. Two possible mechanisms are proposed to account for this difference. Samples made from crystalline boron powders have around an order of magnitude lower Jc compared to those made from amorphous precursors. X-ray, Tc and resistivity studies indicate that this is as a result of reduced current cross section due to the formation of Mg-B-O phases. The samples made from amorphous B contain far fewer Mg-B-O phases than crystalline B despite the fact that the amorphous B contains more B2O3. The different reactivity rates of the precursor powders accounts for this anomaly.
The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link effect betwe
en misaligned grains inside wire and tape conductors. Here we demonstrate a high transport critical current density (Jc) reaching 1.5x10^5 A/cm^2 (Ic = 437 A) at 4.2 K and 10 T in Ba0.6K0.4Fe2As2 (Ba-122) tapes prepared by a combination of conventional powder-in-tube method and optimized hot-press technique. The transport Jc measured at 4.2 K under high magnetic fields of 27 T is still on the level of 5.5x10^4 A/cm^2, which is much higher than those of low-temperature superconductors. This is the first report of hot-pressed Ba-122 superconducting tapes and these Jc values are by far the highest ever reported for iron-based superconducting wires and tapes. These high-performance tapes exhibit high degree of c-axis texture of Ba-122 grains and low anisotropy of transport Jc, showing great potential for construction of high-field superconducting magnets.
The effect of the quality of starting powders on the microstructure and superconducting properties of in-situ processed Fe-sheathed MgB2 tapes has been investigated. Three different types of commercial atomized spherical magnesium powder and two diff
erent purities of amorphous boron powder were employed. When using the 10-micrometre magnesium as precursor powders, the Mg reacted with boron more uniformly and quickly, thus the uniformity of the fabricated MgB2 was improved and the grain size of the MgB2 was decreased, hence significant critical current density (Jc) enhancements were achieved for MgB2 tapes. Jc at 4.2 K for MgB2 tapes made from the 10 um Mg and high purity boron powders was at least a factor of ten higher than values measured for MgB2 samples made from all other starting powders. At 20 K, 5 T, the typical Jc values of the tapes were over 1.0x10^4 A/cm^2 and were much better than those of tape samples reported recently.
The high resistivity of many bulk and film samples of MgB2 is most readily explained by the suggestion that only a fraction of the cross-sectional area of the samples is effectively carrying current. Hence the supercurrent (Jc) in such samples will b
e limited by the same area factor, arising for example from porosity or from insulating oxides present at the grain boundaries. We suggest that a correlation should exist, Jc ~ 1/{Rho(300K) - Rho(50K)}, where Rho(300K) - Rho(50K) is the change in the apparent resistivity from 300 K to 50 K. We report measurements of Rho(T) and Jc for a number of films made by hybrid physical-chemical vapor deposition which demonstrate this correlation, although the reduced effective area argument alone is not sufficient. We suggest that this argument can also apply to many polycrystalline bulk and wire samples of MgB2.