Scanning nano-beam electron diffraction with a pixelated detector was employed to investigate the orientation relationship of nanometer sized, irradiation induced G-phase (M$_6$Ni$_{16}$Si$_{7}$) precipitates in an austenite matrix. Using this detector, the faint diffraction spots originating from the small G-phase particles could be resolved simultaneously as the intense matrix reflections. The diffraction patterns were analyzed using a two-stage template matching scheme, whereby the matrix is indexed first and the precipitates are indexed second after subtraction of the matrix contribution to the diffraction patterns. The results show that G-phase forms with orientation relationships relative to austenite that are characteristic of face-centered cubic (FCC) to body-centered cubic (BCC) transformations. This work demonstrates that nano-beam electron diffraction with a pixelated detector is a promising technique to investigate orientation relationships of nano-sized precipitates with complex crystal structures in other material systems with relative ease.
قيم البحث
اقرأ أيضاً
The rich phase diagram of bulk Pr$_{1-x}$Ca$_{x}$MnO$_3$ resulting in a high tunability of physical properties gave rise to various studies related to fundamental research as well as prospective applications of the material. Importantly, as a consequ
ence of strong correlation effects, electronic and lattice degrees of freedom are vigorously coupled. Hence, it is debatable whether such bulk phase diagrams can be transferred to inherently strained epitaxial thin films. In this paper, the structural orthorhombic to pseudo-cubic transition for $x=0.1$ is studied in ion-beam sputtered thin films and point out differences to the respective bulk system by employing in-situ heating nano-beam electron diffraction to follow the temperature dependence of lattice constants. In addition, it is demonstrated that controlling the environment during heating, i.e. preventing oxygen loss, is crucial in order to avoid irreversible structural changes, which is expected to be a general problem of compounds containing volatile elements under non-equilibrium conditions.
Stress-induced martensitic transformations enable metastable alloys to exhibit enhanced strain hardening capacity, leading to improved formability and toughness. As is well-known from transformation-induced plasticity (TRIP) steels, however, the resu
lting martensite can limit ductility and fatigue life due to its intrinsic brittleness. In this work, we explore an alloy design strategy that utilizes stress-induced martensitic transformations but does not retain the martensite phase. This strategy is based on the introduction of superelastic nano-precipitates, which exhibit reverse transformation after initial stress-induced forward transformation. To this end, utilizing ab-initio simulations and thermodynamic calculations we designed and produced a V45Ti30Ni25 (at%) alloy. In this alloy, TiNi is present as nano-precipitates uniformly distributed within a ductile V-rich base-centered cubic (bcc) beta matrix, as well as being present as a larger matrix phase. We characterized the microstructure of the produced alloy using various scanning electron microscopy (SEM) and transmission electron microscopy (TEM) methods. The bulk mechanical properties of the alloy are demonstrated through tensile tests, and the reversible transformation in each of the TiNi morphologies were confirmed by in-situ TEM micro-pillar compression experiments, in-situ high-energy diffraction synchrotron cyclic tensile tests, indentation experiments, and differential scanning calorimetry experiments. The observed transformation pathways and variables impacting phase stability are critically discussed
Nanoprobe X-ray diffraction (nXRD) using focused synchrotron radiation is a powerful technique to study the structural properties of individual semiconductor nanowires. However, when performing the experiment under ambient conditions, the required hi
gh X-ray dose and prolonged exposure times can lead to radiation damage. To unveil the origin of radiation damage, we compare nXRD experiments carried out on individual semiconductor nanowires in their as grown geometry both under ambient conditions and under He atmosphere at the microfocus station of the P08 beamline at the 3rd generation source PETRA III. Using an incident X-ray beam energy of 9 keV and photon flux of 10$^{10}$s$^{-1}$, the axial lattice parameter and tilt of individual GaAs/In$_{0.2}$Ga$_{0.8}$As/GaAs core-shell nanowires were monitored by continuously recording reciprocal space maps of the 111 Bragg reflection at a fixed spatial position over several hours. In addition, the emission properties of the (In,Ga)As quantum well, the atomic composition of the exposed nanowires and the nanowire morphology are studied by cathodoluminescence spectroscopy, energy dispersive X-ray spectroscopy and scanning electron microscopy, respectively, both prior to and after nXRD exposure. Nanowires exposed under ambient conditions show severe optical and morphological damage, which was reduced for nanowires exposed under He atmosphere. The observed damage can be largely attributed to an oxidation process from X-ray induced ozone reactions in air. Due to the lower heat transfer coefficient compared to GaAs, this oxide shell limits the heat transfer through the nanowire side facets, which is considered as the main channel of heat dissipation for nanowires in the as-grown geometry.
One of the critical milestones in the intensive pursuit of quantitative nanoscale magnetic imaging tools is achieving the level of sensitivity required for detecting the field generated by the spin magnetic moment {mu}B of a single electron. Supercon
ducting quantum interference devices (SQUIDs), which were traditionally the most sensitive magnetometers, could not hitherto reach this goal because of their relatively large effective size (of the order of 1 {mu}m). Here we report self-aligned fabrication of nano-SQUIDs with diameters as small as 46 nm and with an extremely low flux noise of 50 n{Phi}0/Hz^1/2, representing almost two orders of magnitude improvement in spin sensitivity, down to 0.38 {mu}B/Hz^1/2. In addition, the devices operate over a wide range of magnetic fields with 0.6 {mu}B/Hz^1/2 sensitivity even at 1 T. We demonstrate magnetic imaging of vortices in type II superconductor that are 120 nm apart and scanning measurements of AC magnetic fields down to 50 nT. The unique geometry of these nano-SQUIDs that reside on the apex of a sharp tip allows approaching the sample to within a few nm, which paves the way to a new class of single-spin resolved scanning probe microscopy.
Coupling of nano-indentation and crystal plasticity finite element (CPFE) simulations is widely used to quantitatively probe the small-scale mechanical behaviour of materials. Earlier studies showed that CPFE can successfully reproduce the load-displ
acement curves and surface morphology for different crystal orientations. Here, we report the orientation dependence of residual lattice strain patterns and dislocation structures in tungsten. For orientations with one or more Burgers vectors close to parallel to the sample surface, dislocation movement and residual lattice strains are confined to long, narrow channels. CPFE is unable to reproduce this behaviour, and our analysis reveals the responsible underlying mechanisms.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها