Glasses based on SiO2-PbO-CdO-Ga2O3 system have been studied for the first time for fabrication of mid-infrared optical elements. Gallium oxide concentration was gradually increased, replacing silicon dioxide, for different cadmium and lead oxide content. The thermal and optical properties were investigated for different compositions. It was observed that the thermal stability, refractive index, and the transmission in the infrared range increased with increase of gallium and lead concentrations. The most thermally stable glass composition was selected for fabrication of optical elements such as optical fibers. We also successfully fabricated mid-infrared lenses by hot embossing for potential application in compact gas detectors
قيم البحث
اقرأ أيضاً
We present high-reflectivity substrate-transferred single-crystal GaAs/AlGaAs interference coatings at a center wavelength of 4.54 um with record-low excess optical loss below 10 parts per million. These high-performance mirrors are realized via a no
vel microfabrication process that differs significantly from the production of amorphous multilayers generated via physical vapor deposition processes. This new process enables reduced scatter loss due to the low surface and interfacial roughness, while low background doping in epitaxial growth ensures strongly reduced absorption. We report on a suite of optical measurements, including cavity ring-down, transmittance spectroscopy, and direct absorption tests to reveal the optical losses for a set of prototype mirrors. In the course of these measurements, we observe a unique polarization-orientation-dependent loss mechanism which we attribute to elastic anisotropy of these strained epitaxial multilayers. A future increase in layer count and a corresponding reduction of transmittance will enable optical resonators with a finesse in excess of 100 000 in the mid-infrared spectral region, allowing for advances in high resolution spectroscopy, narrow-linewidth laser stabilization, and ultrasensitive measurements of various light-matter interactions.
In this paper, we report the design and fabrication of a highly birefringent polarization-maintaining photonic crystal fiber (PM-PCF) made from chalcogenide glass, and its application to linearly-polarized supercontinuum (SC) generation in the mid-in
frared region. The PM fiber was drawn using the casting method from As38Se62 glass which features a transmission window from 2 to 10 $mu m$ and a high nonlinear index of 1.13.10$^{-17}$m$^{2}$W$^{-1}$. It has a zero-dispersion wavelength around 4.5 $mu m$ and, at this wavelength, a large birefringence of 6.10$^{-4}$ and consequently strong polarization maintaining properties are expected. Using this fiber, we experimentally demonstrate supercontinuum generation spanning from 3.1-6.02 $mu m$ and 3.33-5.78 $mu m$ using femtosecond pumping at 4 $mu m$ and 4.53 $mu m$, respectively. We further investigate the supercontinuum bandwidth versus the input pump polarization angle and we show very good agreement with numerical simulations of the two-polarization model based on two coupled generalized nonlinear Schrodinger equations.
We present measurements of the Faraday effect in n-type InSb. The Verdet coefficient was determined for a range of carrier concentrations near $10^{17}$ $text{cm}^{-3}$ in the $lambda$ = 8 $mu$m - 12 $mu$m long-wave infrared regime. The absorption co
efficient was measured and a figure of merit calculated for each sample. From these measurements, we calculated the carrier effective mass and illustrate the variation of the figure of merit with wavelength. A method for creating a tunable bandpass filter via the Faraday rotation is discussed along with preliminary results from a prototype device.
Metasurfaces offer the potential to control light propagation at the nanoscale for applications in both free-space and surface-confined geometries. Existing metasurfaces frequently utilize metallic polaritonic elements with high absorption losses, an
d/or fixed geometrical designs that serve a single function. Here we overcome these limitations by demonstrating a reconfigurable hyperbolic metasurface comprising of a heterostructure of isotopically enriched hexagonal boron nitride (hBN) in direct contact with the phase-change material (PCM) vanadium dioxide (VO2). Spatially localized metallic and dielectric domains in VO2 change the wavelength of the hyperbolic phonon polaritons (HPhPs) supported in hBN by a factor 1.6 at 1450cm-1. This induces in-plane launching, refraction and reflection of HPhPs in the hBN, proving reconfigurable control of in-plane HPhP propagation at the nanoscale15. These results exemplify a generalizable framework based on combining hyperbolic media and PCMs in order to design optical functionalities such as resonant cavities, beam steering, waveguiding and focusing with nanometric control.
Recently, in-plane biaxial hyperbolicity has been observed in $alpha$-MoO${_3}$ --a van der Waal crystal-- in the mid-infrared frequency regime. Here, we present a comprehensive theoretical analysis of thin film $alpha$-MoO${_3}$ for application to t
wo mid-IR photonic devices -- a polarizer and a waveplate. We show the possibility of a significant reduction in the device footprint while maintaining an enormous extinction ratio from $alpha$-MoO${_3}$ based polarizers in comparison with that of conventional polarizers. Secondly, we carry out device optimization of $alpha$-MoO${_3}$ based waveplates with subwavelength thickness. We explain our results using natural in-plane hyperbolicity of $alpha$-MoO${_3}$ via analytical and full wave simulations. This work will build a foundation for miniaturization of mid-infrared photonic devices by exploiting the optical anisotropy of $alpha$-MoO${_3}$.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها