تسجيل مستخدم جديدStudy of soft/hard bimagnetic CoFe2/CoFe2O4 nanocomposite
68
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report an experimental study of the bimagnetic nanocomposites CoFe2/CoFe2O4.The precursor material, CoFe2O4 was prepared using the conventional stoichiometric combustion method. The nanocomposite CoFe2/CoFe2O4 was obtained by total reduction of CoFe2O4 using a thermal treatment at 350oC in H2 atmospheres following a partial oxidation in O2 atmospheres at 380oC during 120; 30; 15, 10, and 5 min. The X-ray diffraction and Mossbauer spectroscopy confirmed the formation the material CoFe2/CoFe2O4 The magnetic hysteresis with different saturation magnetization confirms the formation of the CoFe2/CoFe2O4 with different content of CoFe2O4. The high energy milling to the precursor material increase the coercivity from 1.0 to 3.3 kOe, however the same effect was not observed to the CoFe2/CoFe2O4 material.
قيم البحث
اقرأ أيضاً
In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe2O4 and ferrimagnetic oxide/ferromagnetic metal CoFe2O4/CoFe2 nanocomposites. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange
coupling. Two steps were used to synthesize the bimagnetic CoFe2O4/CoFe2 nanocomposites: (i) first preparation of CoFe2O4 nanoparticles using the a simple hydrothermal method and (ii) second reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe2O4 nanoparticles have been investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50K. The mean diameter of CoFe2O4 particles is about 16 nm. Mossbauer spectra reveal two sites for Fe3+. One site is related to Fe in an octahedral coordination and the other one to the Fe3+ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe2O4. TEM measurements of nanocomposite show the formation of a thin shell of CoFe2 on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of nanocomposite showed hysteresis loop that is characteristic of the exchange spring systems. A maximum energy product (BH)max of 1.22 MGOe was achieved at room temperature for CoFe2O4/CoFe2 nanocomposites, which is about 115% higher than the value obtained for CoFe2O4 precursor. The exchange-spring interaction and the enhancement of product (BH)max in nanocomposite CoFe2O4/CoFe2 have been discussed.
The nanoscale distribution of magnetic anisotropies was measured in core@shell MnFe$_2$O$_4$@CoFe$_2$O$_4$ 7.0 nm particles using a combination of element selective magnetic spectroscopies with different probing depths. As this picture is not accessi
ble by any other technique, emergent magnetic properties were revealed. The coercive field is not constant in a whole nanospinel. The very thin (0.5 nm) CoFe$_2$O$_4$ hard shell imposes a strong magnetic anisotropy to the otherwise very soft MnFe$_2$O$_4$ core: a large gradient in coercivity was measured inside the MnFe$_2$O$_4$ core with lower values close to the interface region, while the inner core presents a substantial coercive field (0.54 T) and a very high remnant magnetization (90% of the magnetization at saturation).
We study spin wave excitations in a three-dimensional nanocomposite magnet of exchange coupled hard (SmCo$_5$) and soft (FeCo) phases. The dipolar interaction splits the spin wave energies into the upper and lower branches of the spin wave manifold.
When the amount of the soft phase is increased the energy of low-lying spin excitations is considerably softened due to two reasons: (i) the low- lying mode locked into the soft phase region with a spin wave gap at ${bf k}= 0$ which scales approximately proportional to the anisotropy constant of the soft phase and (ii) the internal dipolar field which comes from magnetic charges forming at hard-soft boundaries with normals parallel to the magnetization displaces the spin wave manifold toward the lower energies. With adding more soft phase the spin wave gap closes and the system moves to another ground state characterized by the magnetization mismatch between spins of the hard and soft phases.
We observe the magnetic proximity effect (MPE) in Pt/CoFe2O4 bilayers grown by molecular beam epitaxy. This is revealed through angle-dependent magnetoresistance measurements at 5 K, which isolate the contributions of induced ferromagnetism (i.e. ani
sotropic magnetoresistance) and spin Hall effect (i.e. spin Hall magnetoresistance) in the Pt layer. The observation of induced ferromagnetism in Pt via AMR is further supported by density functional theory calculations and various control measurements including insertion of a Cu spacer layer to suppress the induced ferromagnetism. In addition, anomalous Hall effect measurements show an out-of-plane magnetic hysteresis loop of the induced ferromagnetic phase with larger coercivity and larger remanence than the bulk CoFe2O4. By demonstrating MPE in Pt/CoFe2O4, these results establish the spinel ferrite family as a promising material for MPE and spin manipulation via proximity exchange fields.
The strain dependence of electric and magnetic properties has been widely investigated, both from a fundamental science perspective and an applications point of view. Electromechanical coupling through field-induced polarization rotation (PRO) and po
larization reorientation (PRE) in piezoelectric single crystals can provide an effective strain in film/substrate epitaxial heterostructures. However, the specific pathway of PRO and PRE is a complex thermodynamic process, depending on chemical composition, temperature, electric field and mechanical load. Here, systematic studies of the temperature-dependent field-induced phase transitions in Pb(Mg,Nb)O3-PbTiO3 single crystals with different initial phase and orientation configurations have been performed. Different types of strains, volatile/nonvolatile and biaxial/uniaxial, have been measured by both macroscopic and in-situ X-ray diffraction techniques. In addition, the strain state of epitaxial Mn-doped CoFe2O4 thin films was examined by magnetic anisotropy measurements, where a giant magnetoelectric coupling has been demonstrated.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها