We have carried out detailed magnetic and transport studies of the new Sr0.5Ce0.5FBiS2-xSex (x = 0.5, 1) superconductors derived by doping Se in Sr0.5Ce0.5FBiS2. Se-doping produces several effects: it suppresses semiconducting like behavior observed in the undoped Sr0.5Ce0.5FBiS2, ferromagnetic ordering temperature, TFM, decreases considerably from 7.5 K (in Sr0.5Ce0.5FBiS2) to 3.5 K and superconducting transition temperature, Tc, gets enhanced slightly to 2.9 - 3.3 K. Thus in these Se-doped materials, TFM is just marginally higher than Tc. Magnetization studies provide an evidence of bulk superconductivity in Sr0.5Ce0.5FBiS2-xSex. Quite remarkably, as compared with the effective paramagnetic Ce-moment (~ 2.2 muB), the ferromagnetically ordered Ce-moment in the superconducting state is rather small (~ 0.1 muB). To the best of our knowledge, the title compounds are the first Ce-based superconducting itinerant ferromagnetic materials (Tc < TFM). We stress that Ce-4f electrons are responsible for both superconductivity and ferromagnetism just as U-5f electrons are in UCoGe. Furthermore, a novel feature of these materials is a dual hysteresis loop corresponding to both the ferromagnetism and the coexisting superconductivity. Such features of Sr0.5Ce0.5FBiS2-xSex put these materials apart from the well known U-containing superconducting ferromagnets reported so far.
قيم البحث
اقرأ أيضاً
The compound Sr$_{0.5}$Ce$_{0.5}$FBiS$_{2}$ belongs to the intensively studied family of layered BiS$_2$ superconductors. It attracts special attention because superconductivity at $T_{sc} = 2.8$ K was found to coexist with local-moment ferromagnetic
order with a Curie temperature $T_C = 7.5$ K. Recently it was reported that upon replacing S by Se $T_C$ drops and ferromagnetism becomes of an itinerant nature (Thakur et al., Sci. Reports 6, 37527 (2016)). At the same time $T_{sc}$ increases and it was argued superconductivity coexists with itinerant ferromagnetism. Here we report a muon spin rotation and relaxation study ($mu$SR) conducted to investigate the coexistence of superconductivity and ferromagnetic order in Sr$_{0.5}$Ce$_{0.5}$FBiS$_{2-x}$Se$_x$ with $x=0.5$ and $1.0$. By inspecting the muon asymmetry function we find that both phases do not coexist on the microscopic scale, but occupy different sample volumes. For $x=0.5$ and $x=1.0$ we find a ferromagnetic volume fraction of $sim , 8 %$ and $sim , 30 %$ at $T=0.25$ K, well below $T_{C} = 3.4$ K and $T_C = 3.3$ K, respectively. For $x=1.0$ ($T_{sc} = 2.9$ K) the superconducting phase occupies the remaining sample volume ($sim , 70 %$), as shown by transverse field experiments that probe the Gaussian damping due to the vortex lattice. We conclude ferromagnetism and superconductivity are macroscopically phase separated.
Superconducting characteristics such as the Meissner-Ochsenfeld state, screening supercurrents and hysteresis loops of type-II superconductors were observed from the temperature and magnetic field dependences of the magnetic moment, m(T, H), in graph
ite powders reacted with sulfur for temperatures below 9.0 K. The temperature dependence of the lower critical field Hc1(T) was determined and the zero-temperature penetration depth, lambda(0), was estimated (lambda (0) = 227 nm). The superconductivity was observed to be highly anisotropic and to coexist with a ferromagnetic state that has a Curie temperature well above room temperature. A continuous transition from the superconducting state to the ferromagnetic state could be achieved by simply increasing the applied magnetic field.
We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respec
tive magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the substitution of O by F are supplied to not only the BiS2 superconducting layers but also the CeO blocking layers. Furthermore, the highest superconducting transition temperature is observed when the ferromagnetism is also enhanced, which implies that superconductivity and ferromagnetism are linked to each other in the CeO1-xFxBiS2 system.
The magnetic structure of the Eu2+ moments in the superconducting EuFe2(As1-xPx)2 sample with x = 0.15 has been determined using element specific x-ray resonant magnetic scattering. Combining magnetic, thermodynamic and scattering measurements, we co
nclude that the long range ferromagnetic order of the Eu2+ moments aligned primarily along the c axis coexists with the bulk superconductivity at zero field. At an applied magnetic field >= 0.6 T, superconductivity still coexists with the ferromagnetic Eu2+ moments which are polarized along the field direction. We propose a spontaneous vortex state for the coexistence of superconductivity and ferromagnetism in EuFe2(As0.85P0.15)2.
Unambiguous evidence for the microscopic coexistence of ferromagnetism and superconductivity in UCoGe ($T_{rm Curie} sim 2.5$ K and $T_{rm SC}$ $sim$ 0.6 K) is reported from $^{59}$Co nuclear quadrupole resonance (NQR). The $^{59}$Co-NQR signal below
1 K indicates ferromagnetism throughout the sample volume, while nuclear spin-lattice relaxation rate $1/T_1$ in the ferromagnetic (FM) phase decreases below $T_{rm SC}$ due to the opening of the superconducting(SC) gap. The SC state was found to be inhomogeneous, suggestive of a self-induced vortex state, potentially realizable in a FM superconductor. In addition, the $^{59}$Co-NQR spectrum around $T_{rm Curie}$ show that the FM transition in UCoGe possesses a first-order character, which is consistent with the theoretical prediction that the low-temperature FM transition in itinerant magnets is generically of first-order.