تسجيل مستخدم جديدAnisotropic transverse magnetoresistivity in alpha-YbAlB4
86
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We measured the transverse magnetoresistivity of the mixed valence compound $alpha$-YbAlB$_4$. Two configurations were used where current was applied along [110] direction for both and magnetic field was applied along [-110] and $c$-axis. We found the transverse magnetoresistivity is highly anisotropic. In the weak field below 1 T, it is consistent with stronger $c$-$f$ hybridization in the $ab$ plane which was suggested from the previous zero field resistivity measurements. At the higher field above 3 T, we observed a negative transverse magnetoresistivity for the field applied along the $c$-axis. The temperature dependences of the resistivity measured at several different fields suggest the suppression of the heavy fermion behavior at the characteristic field of $sim 5.5$ T.
قيم البحث
اقرأ أيضاً
The intermediate-valent polymorphs $alpha$- and $beta$-YbAlB$_4$ exhibit quantum criticality and other novel properties not usually associated with intermediate valence. Iron doping induces quantum criticality in $alpha$-YbAlB$_4$ and magnetic order
in both compounds. We report results of muon spin relaxation ($mu$SR) experiments in the intermediate-valent alloys $alpha$-YbAl$_{1-x}$Fe$_x$B$_4$, $x = 0.014$ and 0.25. For $x = 0.014$ we find no evidence for magnetic order down to 25 mK@. The dynamic muon spin relaxation rate $lambda_d$ exhibits a power-law temperature dependence $lambda_d propto T^{-a}$, $a = 0.40(4)$, in the temperature range 100 mK--2 K, in disagreement with predictions by theories of antiferromagnetic (AFM) or valence quantum critical behavior. For $x = 0.25$, where AFM order develops in the temperature range 7.5--10 K, where we find coexistence of meso- or macroscopically segregated paramagnetic and AFM phases, with considerable disorder in the latter down to 2 K.
Phonon dispersion of detwinned NiO is measured using inelastic x-ray scattering. It is found that, near the zone center, the energy of the transverse optical phonon mode polarized parallel to the antiferromagnetic order is ~1 meV lower than that of t
he mode polarized perpendicular to the order, at room temperature. This is explained via anisotropic polarization of the Ni and O atoms, as confirmed using a Berrys phase approach with first-principles calculations. Our explanation avoids an apparent contradiction in previous discussions focusing on Heisenberg interaction.
The laminar perovskite Ca3Ru2O7 naturally forms ferromagnetic double-layers of alternating moment directions, as in the spin-valve superlattices. The mechanism of huge magnetoresistive effect in the material has been controversial due to a lack of cl
ear understanding of various magnetic phases and phase-transitions. In this neutron diffraction study in a magnetic field, we identify four different magnetic phases in Ca3Ru2O7 and determine all first-order and second-order phase transitions between them. The spin-valve mechanism then readily explains the dominant magnetoresistive effect in Ca3Ru2O7.
The in-plane ($rho_{ab}$) and c-axis ($rho_c$) resistivities, and the magnetoresistivity of single crystals $Na_xCoO_2$ with x = 0.7, 0.5 and 0.3 were studied systematically. $rho_{ab}(T)$ shows similar temperature dependence between $Na_{0.3}CoO_2$
and $Na_{0.7}CoO_2$, while $rho_c(T)$ is quite different. A dimensional crossover from two to three occurs with decreasing Na concentration from 0.7 to 0.3. The angular dependence of in-plane magnetoresistivity for 0.5 sample shows a emph{d-wave-like} symmetry at 2K, while the emph{p-wave-like} symmetry at 20 K. These results give an evidence for existence of a emph{spin ordering orientation} below 20 K turned by external field, like the stripes in cuprates.
The valence state of Yb ions in beta-YbAlB4 and its polymorph alpha-YbAlB4 has been investigated by using X-ray absorption and emission spectroscopy in SPring-8 at temperatures from 2 to 280 K. The observed Yb valence is 2.78 +- 0.01 in beta-YbAlB4 a
t 2 K by using the X-ray emission spectroscopy. The valence is found to gradually increase with increasing temperature toward the trivalent state, and the characteristic temperature of the valence fluctuation is expected to be about 290 K. We also found a small increase in the Yb valence (~0.002) by applying a magnetic field of 32 T at 40 K to beta-YbAlB4.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها