تسجيل مستخدم جديدOrbital magnetic moment and coercivity of SiO$_{2}$-coated FePt nanoparticles studied by x-ray magnetic circular dichroism
316
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have investigated the spin and orbital magnetic moments of Fe in FePt nanoparticles in the $L$1$_{0}$-ordered phase coated with SiO$_{2}$ by x-ray absorption spectroscopy (XAS) and x-ray magnetic circular dichroism (XMCD) measurements at the Fe $L_{rm 2,3}$ absorption edges. Using XMCD sum rules, we evaluated the ratio of the orbital magnetic moment ($M_{rm orb}$) to the spin magnetic moment ($M_{rm spin}$) of Fe to be $M_{rm orb}/M_{rm spin}$ = 0.08. This $M_{rm orb}/M_{rm spin}$ value is comparable to the value (0.09) obtained for FePt nanoparticles prepared by gas phase condensation, and is larger than the values ($sim$0.05) obtained for FePt thin films, indicating a high degree of $L$1$_{0}$ order. The hysteretic behavior of the FePt component of the magnetization was measured by XMCD. The magnetic coercivity ($H_{rm c}$) was found to be as large as 1.8 T at room temperature, $sim$3 times larger than the thin film value and $sim$50 times larger than that of the gas phase condensed nanoparticles. The hysteresis curve is well explained by the Stoner-Wohlfarth model for non-interacting single-domain nanoparticles with the $H_{rm c}$ distributed from 1 T to 5 T.
قيم البحث
اقرأ أيضاً
The strong perpendicular magnetic anisotropy of $L{rm1_0}$-ordered FePt has been the subject of extensive studies for a long time. However, it is not known which element, Fe or Pt, mainly contributes to the magnetic anisotropy energy (MAE). We have i
nvestigated the anisotropy of the orbital magnetic moments of Fe 3$d$ and Pt 5$d$ electrons in $L{rm1_0}$-ordered FePt thin films by Fe and Pt $L_{2,3}$-edge x-ray magnetic circular dichroism (XMCD) measurements for samples with various degrees of long-range chemical order $S$. Fe $L_{2,3}$-edge XMCD showed that the orbital magnetic moment was larger when the magnetic field was applied perpendicular to the film than parallel to it, and that the anisotropy of the orbital magnetic moment increased with $S$. Pt $L_{2,3}$-edge XMCD also showed that the orbital magnetic moment was smaller when the magnetic field was applied perpendicular to the film than parallel to it, opposite to the Fe $L_{2,3}$-edge XMCD results although the anisotropy of the orbital magnetic moment increases with $S$ like the Fe edge. These results are qualitatively consistent with the first-principles calculation by Solovyev ${it et al.}$ [Phys. Rev. B $bf{52}$, 13419 (1995).], which also predicts the dominant contributions of Pt 5$d$ to the magnetic anisotropy energy rather than Fe 3$d$ due to the strong spin-orbit coupling and the small spin splitting of the Pt 5$d$ bands in $L{rm1_0}$-ordered FePt.
The electric-field control of $d$-electron magnetism in multiferroic transition metal oxides is attracting widespread interest for the underlying fundamental physics and for next generation spintronic devices. Here, we report an extensive study of th
e $3d$ magnetism in magnetoelectric Ga$_{0.6}$Fe$_{1.4}$O$_3$ (GFO) epitaxial films by polarization dependent x-ray absorption spectroscopy. We found a non-zero integral of the x-ray magnetic circular dichroism, with a sign depending upon the relative orientation between the external magnetic field and the crystallographic axes. %By reliably enlarging the limit of the spin and orbital sum rules, which usually holds for materials where the magnetic ions exhibit a unique crystal field symmetry This finding translates in a sign-reversal between the average Fe magnetic orbital and spin moments. Large Fe-displacements, among some of the octahedral sites, lower the symmetry of the system producing anisotropic paths for the Fe-O bondings giving rise to a large orbital-lattice interaction akin to a preferential crystallographic direction for the magnetic orbital moment. The latter may lead to a partial re-orientation of the magnetic orbital moment under an external magnetic field that, combined to the ferrimagnetic nature of the GFO, can qualitatively explain the observed sign-reversal of the XMCD integral. The results suggest that a control over the local symmetry of the oxygen octahedra in transition metal oxides can offer a suitable leverage over the manipulation of the effective orbital and spin moments in magnetoelectric systems.
We have investigated the electronic structure of ZnO:Mn and ZnO:Mn,N thin films using x-ray magnetic circular dichroism (XMCD) and resonance-photoemission spectroscopy. From the Mn 2$p$$rightarrow3d$ XMCD results, it is shown that, while XMCD signals
only due to paramagnetic Mn$^{2+}$ ions were observed in ZnO:Mn, nonmagnetic, paramagnetic and ferromagnetic Mn$^{2+}$ ions coexist in ZnO:Mn,N. XMCD signals of ZnO:Mn,N revealed that the localized Mn$^{2+}$ ground state and Mn$^{2+}$ state hybridized with ligand hole coexisted, implying $p$-$d$ exchange coupling. In the valence-band spectra, spectral weight near the Fermi level was suppressed, suggesting that interaction between magnetic moments in ZnO:Mn,N has localized nature.
The magnetic properties of as-grown Ga$_{1-x}$Mn$_{x}$As have been investigated by the systematic measurements of temperature and magnetic field dependent soft x-ray magnetic circular dichroism (XMCD). The {it intrinsic} XMCD intensity at high temper
atures obeys the Curie-Weiss law, but residual spin magnetic moment appears already around 100 K, significantly above Curie temperature ($T_C$), suggesting that short-range ferromagnetic correlations are developed above $T_C$. The present results also suggest that antiferromagnetic interaction between the substitutional and interstitial Mn (Mn$_{int}$) ions exists and that the amount of the Mn$_{int}$ affects $T_C$.
BiFeO$_3$ (BFO) shows both ferroelectricity and magnetic ordering at room temperature but its ferromagnetic component, which is due to spin canting, is negligible. Substitution of transition-metal atoms such as Co for Fe is known to enhance the ferro
magnetic component in BFO. In order to reveal the origin of such magnetization enhancement, we performed soft x-ray absorption spectroscopy (XAS) and soft x-ray magnetic circular dichroism (XMCD) studies of BiFe$_{1-x}$Co$_x$O$_3$ ({it x} = 0 to 0.30) (BFCO) thin films grown on LaAlO$_3$(001) substrates. The XAS results indicated that the Fe and Co ions are in the Fe$^{3+}$ and Co$^{3+}$ states. The XMCD results showed that the Fe ions show ferromagnetism while the Co ions are antiferromagnetic at room temperature. The XAS and XMCD measurements also revealed that part of the Fe$^{3+}$ ions are tetrahedrally co-ordinated by oxygen ions but that the XMCD signals of the octahedrally coordinated Fe$^{3+}$ ions increase with Co content. The results suggest that an impurity phase such as the ferrimagnetic $gamma$-Fe$_2$O$_3$ which exists at low Co concentration decreases with increasing Co concentration and that the ferromagnetic component of the Fe$^{3+}$ ion in the octrahedral crystal fields increases with Co concentration, probably reflecting the increased canting of the Fe$^{3+}$ ions.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها