تسجيل مستخدم جديدCharacterization of Fe-N nano crystals and nitrogen-containing inclusions in (Ga,Fe)N thin films using transmission electron microscopy
139
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Nanometric inclusions filled with nitrogen, located adjacent to FenN (n = 3 or 4) nanocrystals within (Ga,Fe)N layers, are identified and characterized using scanning transmission electron microscopy (STEM) and electron energy-loss spectroscopy (EELS). High-resolution STEM images reveal a truncation of the Fe-N nanocrystals at their boundaries with the nitrogen-containing inclusion. A controlled electron beam hole drilling experiment is used to release nitrogen gas from an inclusion in situ in the electron microscope. The density of nitrogen in an individual inclusion is measured to be 1.4 +- 0.3 g/cm3. These observations provide an explanation for the location of surplus nitrogen in the (Ga,Fe)N layers, which is liberated by the nucleation of FenN (n> 1) nanocrystals during growth.
قيم البحث
اقرأ أيضاً
We employ x-ray spectroscopy to characterize the distribution and magnetism of particular alloy constituents in (Ga,Fe)N films grown by metal organic vapor phase epitaxy. Furthermore, photoelectron microscopy gives direct evidence for the aggregation
of Fe ions, leading to the formation of Fe-rich nanoregions adjacent to the samples surface. A sizable x-ray magnetic circular dichroism (XMCD) signal at the Fe L-edges in remanence and at moderate magnetic fields at 300 K links the high temperature ferromagnetism with the Fe(3d) states. The XMCD response at the N K-edge highlights that the N(2p) states carry considerable spin polarization. We conclude that FeN{delta} nanocrystals, with delta > 0.25, stabilize the ferromagnetic response of the films.
Magnetooptical properties of (Ga,Mn)N layers containing various concentrations of Fe-rich nanocrystals embedded in paramagnetic (Ga,Fe)N layers are reported. Previous studies of such samples demonstrated that magnetization consists of a paramagnetic
contribution due to substitutional diluted Fe ions as well as of ferromagnetic and antiferromagnetic components originating from Fe-rich nanocrystals, whose relative abundance can be controlled by the grow conditions. The nanocrystals are found to broaden and to reduce the magnitude of the excitonic features. However, the ferromagnetic contribution, clearly seen in SQUID magnetometry, is not revealed by magnetic circular dichroism (MCD). Possible reasons for differences in magnetic response determined by MCD and SQUID measurements are discussed.
We show that by introducing isoelectronic iron (Fe) magnetic impurities and Beryllium (Be) double-donor atoms into InAs, it is possible to grow a n-type ferromagnetic semiconductor (FMS) with the ability to control ferromagnetism by both Fe and indep
endent carrier doping by low-temperature molecular-beam epitaxy. We demonstrate that (In,Fe)As doped with electrons behaves as an n-type electron-induced FMS. This achievement opens the way to realize novel spin-devices such as spin light-emitting diodes or spin field-effect transistors, as well as helps understand the mechanism of carrier-mediated ferromagnetism in FMSs.
Room temperature ferromagnetism was observed in n-type Fe-doped In2O3 thin films deposited on c-cut sapphire substrates by pulsed laser deposition. Structure, magnetism, composition, and transport studies indicated that Fe occupied the In sites of th
e In2O3 lattice rather than formed any metallic Fe or other magnetic impurity phases. Magnetic moments of films were proved to be intrinsic and showed to have a strong dependence on the carrier densities which depended on the Fe concentration and its valance state as well as oxygen pressure.
Tetragonal Mn$_x$Ga$_{1-x}$ (x=0.70, 0.75) thin films grown on SrTiO$_3$ substrates at different temperatures and thicknesses exhibit perpendicular magnetic anisotropy with coercive fields between 1-2 T. Transmission electron microscopy (TEM) and X-r
ay diffraction (XRD) reveal that 40nm samples grown at 300-350$^{o}$C lead to polycrystalline films with the tetragonal c-axis oriented primarily perpendicular to the film plane but with some fraction of the sample exhibiting the c-axis in the film plane. This structure results in a secondary magnetic component in the out of plane magnetization. Growth at 300$^{o}$C with a reduced thickness or Mn concentration significantly decreases the presence of the tetragonal c-axis in the film plane, thus improving the magnetic properties. TEM is of critical importance in characterizing these materials, since conventional XRD cannot always identify the presence of additional crystallographic orientations although they can still affect the magnetic properties. Our study points to ways that the microstructure of these thin films can be controlled, which is critical for utilization of this material in spintronic devices.