We realize growth of self-catalyzed core-shell GaAs/GaAsP nanowires (NWs) on Si substrates using molecular-beam epitaxy. Transmission electron microscopy (TEM) of single GaAs/GaAsP NWs confirms their high crystal quality and shows domination of the zinc-blende phase. This is further confirmed in optics of single NWs, studied using cw and time-resolved photoluminescence (PL). A detailed comparison with uncapped GaAs NWs emphasizes the effect of the GaAsP capping in suppressing the non-radiative surface states: significant PL enhancement in the core-shell structures exceeding 2000 times at 10K is observed; in uncapped NWs PL is quenched at 60K whereas single core-shell GaAs/GaAsP NWs exhibit bright emission even at room temperature. From analysis of the PL temperature dependence in both types of NW we are able to determine the main carrier escape mechanisms leading to the PL quench.
قيم البحث
اقرأ أيضاً
It is well known that the crystalline structure of the III-V nanowires (NWs) is mainly controlled by the wetting contact angle of the catalyst droplet which can be tuned by the III and V flux. In this work we present a method to control the wurtzite
(WZ) or zinc-blende (ZB) structure in self-catalyzed GaAs NWs grown by molecular beam epitaxy, using in situ reflection high energy electron diffraction (RHEED) diagram analysis. Since the diffraction patterns of the ZB and WZ structures differ according to the azimuth [1-10], it is possible to follow the evolution of the intensity of specific ZB and WZ diffraction spots during the NW growth as a function of the growth parameters such as the Ga flux. By analyzing the evolution of the WZ and ZB spot intensities during some NW growths with specific changes of Ga flux, it is then possible to control the crystal structure of the NWs. ZB GaAs NWs with a controlled WZ segment have thus been realized. Using a semi-empirical model for the NW growth and our in situ RHEED measurements, the critical wetting angle of the catalyst droplet for the structural transition is deduced.
We study the optical properties of a single core-shell GaAs-AlGaAs nanowire (grown by VLS method) using the technique of micro-photoluminescence and spatially-resolved photoluminescence imaging. We observe large linear polarization anisotropy in emission and excitation of nanowires.
We report observation of field emission from self-catalyzed GaAs nanowires grown on Si (111). The measurements are realized inside a scanning electron microscope chamber with nano-controlled tungsten tip functioning as anode. Experimental data are an
alyzed in the framework of Fowler-Nordheim theory. We demonstrate stable current up to 10$^{-7}$ A emitted from the tip of single nanowire, with field enhancement factor $beta$ up to 112 at anode-cathode distance d=350 nm. A linear dependence of $beta$ on the anode-cathode distance is experimentally found. We also show that the presence of a Ga catalyst droplet suppresses the emission of current from the nanowire tip. This allows detection of field emission from the nanowire sidewalls, which occurs with reduced field enhancement factor and stability. This study further extends the GaAs technology to vacuum electronics applications.
Core-shell nanowires made of Si and Ge can be grown experimentally with excellent control for different sizes of both core and shell. We have studied the structural properties of Si/Ge and Ge/Si core-shell nanowires aligned along the $[110]$ directio
n, with diameters up to 10.2~nm and varying core to shell ratios, using linear scaling Density Functional Theory (DFT). We show that Vegards law, which is often used to predict the axial lattice constant, can lead to an error of up to 1%, underlining the need for a detailed emph{ab initio} atomistic treatment of the nanowire structure. We analyse the character of the intrinsic strain distribution and show that, regardless of the composition or bond direction, the Si core or shell always expands. In contrast, the strain patterns in the Ge shell or core are highly sensitive to the location, composition and bond direction. The highest strains are found at heterojunction interfaces and the surfaces of the nanowires. This detailed understanding of the atomistic structure and strain paves the way for studies of the electronic properties of core-shell nanowires and investigations of doping and structure defects.
Optically active gold-catalyzed ZnTe nanowires have been grown by molecular beam epitaxy, on a ZnTe(111) buffer layer, at low temperature 350degree under Te rich conditions, and at ultra-low density (from 1 to 5 nanowires per micrometer^{2}. The crys
talline structure is zinc blende as identified by transmission electron microscopy. All nanowires are tapered and the majority of them are <111> oriented. Low temperature micro-photoluminescence and cathodoluminescence experiments have been performed on single nanowires. We observe a narrow emission line with a blue-shift of 2 or 3 meV with respect to the exciton energy in bulk ZnTe. This shift is attributed to the strain induced by a 5 nm-thick oxide layer covering the nanowires, and this assumption is supported by a quantitative estimation of the strain in the nanowires.