تسجيل مستخدم جديدAnisotropy of the coherence length from critical currents in the stoichiometric superconductor LiFeAs
135
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Miniature Hall-probe arrays were used to measure the critical current densities for the three main directions of vortex motion in the stoichiometric LiFeAs superconductor. These correspond to vortices oriented along the c-axis moving parallel to the ab-plane, and to vortices in the ab-plane moving perpendicular to, and within the plane, respectively. The measurements were carried out in the low-field regime of strong vortex pinning, in which the critical current anisotropy is solely determined by the coherence length anisotropy parameter, {epsilon}_{xi}. This allows extraction of {epsilon}_{xi} at magnetic fields far below the upper critical field B_c2. We find that increasing magnetic field decreases the anisotropy of the coherence length.
قيم البحث
اقرأ أيضاً
The upper critical field $mu_0H_{c2}(T_c)$ of LiFeAs single crystals has been determined by measuring the electrical resistivity using the facilities of pulsed magnetic field at Los Alamos. We found that $mu_0H_{c2}(T_c)$ of LiFeAs shows a moderate a
nisotropy among the layered iron-based superconductors; its anisotropic parameter $gamma$ monotonically decreases with decreasing temperature and approaches $gammasimeq 1.5$ as $Trightarrow 0$. The upper critical field reaches 15T ($Hparallel c$) and 24.2T ($Hparallel ab$) at $T=$1.4K, which value is much smaller than other iron-based high $T_c$ superconductors. The temperature dependence of $mu_0H_{c2}(T_c)$ can be described by the Werthamer-Helfand-Hohenberg (WHH) method, showing orbitally and (likely) spin-paramagnetically limited upper critical field for $Hparallel c$ and $Hparallel ab$, respectively.
Field and temperature microwave measurements have been carried out on MgB2 thin film grown on Al2O3 substrate. The analysis reveals the mean field coherence length xi_{MF} in the mixed state and a temperature independent anisotropy ratio gamma_{MF} =
xi_{MF}^{ab} / xi_{MF}^c approximately 2. At the superconducting transition, the scaling of the fluctuation conductivity yields the Ginzburg-Landau coherence length with a different anisotropy ratio gamma_{GL} = 2.8, also temperature independent.
The magnetic properties of LiFeAs, as single crystalline and polycrystalline samples, were investigated. The lower critical field deduced from the vortex penetration of two single crystals appears to be almost isotropic with a temperature dependence
closer to that of two-gap superconductors. The parameters extracted from the reversible magnetizations of sintered polycrystalline samples are in good agreement with those from the single crystal data.
Using small-angle neutron scattering, we have studied the flux-line lattice (FLL) in superconducting CeCoIn5. The FLL is found to undergo a first-order symmetry and reorientation transition at ~0.55 T at 50 mK. The FLL form factor in this material is
found to be independent of the applied magnetic field, in striking contrast to the exponential decrease usually observed in superconductors. This result is consistent with a strongly field-dependent coherence length in CeCoIn5, in agreement with recent theoretical predictions for superclean, high-kappa superconductors.
Superconducting ($S$) thin film superlattices composed of Nb and a normal metal spacer ($N$) have been extensively utilized in Josephson junctions given their favorable surface roughness compared to Nb films of comparable thickness. In this work, we
characterize the London penetration depth and Ginzburg-Landau coherence lengths of $S/N$ superlattices using polarized neutron reflectometry and electrical transport. Despite the normal metal spacer layers being only approximately 8% of the total superlattice thickness, we surprisingly find that the introduction of these thin $N$ spacers between $S$ layers leads to a dramatic increase in the measured London penetration depth compared to that of a single Nb film of comparable thickness. Using the measured values for the effective in- and out-of-plane coherence lengths, we quantify the induced anisotropy of the superlattice samples and compare to a single Nb film sample. From these results, we find that that the superlattices behave similarly to layered 2D superconductors.